The invention relates to firewood-fired porcelain yellow glaze. The firewood-fired porcelain yellow glazeis prepared from the following components in parts by weight: 20.18 parts of quartz, 33.23 parts of feldspar, 11.26 parts of calcite, 2.05 parts of talc, 18.83 parts of lime, 5.58 parts of phosphorus bone powder, 3.48 parts of agate stone, 2.56 parts of water bone stone and 2.83 parts of white metal soil; quartz sand is adopted as the quartz, the content of quartz in the quartz sand is greater than or equal to 90%; the feldspar is one or a combination of albite and potassium feldspar; and the phosphorus bone powder is any one of cattle bone powder, pig bone powder or horse bone powder, and the content of phosphorus is greater than or equal to 14.5%. The preparation method comprises the following steps of: step 1, green body preparation, specifically, preparing a green body for later use; step 2, grinding, specifically, weighing the components of the glaze according to the formula, and adding the materials into a Raymond mill for grinding; step 3, biscuit firing, specifically, performing biscuit firing to obtain a biscuit firing blank for use; step 4, glazing, specifically, glazing the biscuit firing blank; and step 5, firing, specifically, firing the glazed biscuit firing blank. The preparation process of the firewood-fired porcelain yellow glaze is reasonable, has good glossiness and is stable and free of color blocks.
本发明涉及柴瓷谷黄釉，它是由各组分按照以下重量配比制成：石英20.18份、长石33.23份、方解石11.26份、滑石2.05份、青灰18.83份、磷骨粉5.58份、玛瑙石3.48份、水骨石2.56份、乌金土2.83份，石英采用的是石英砂，石英砂中石英的含量≥90%，长石为钠长石和钾长石中的一种或两种的组合，磷骨粉为牛骨粉、猪骨粉或马骨粉中任意一种，其中磷的含量≥14.5%；它的制成包括以下步骤：步骤1、坯体制备：制备坯体备用；步骤2、磨粉，按配方称取釉料的各组分，通将物料加入到雷蒙磨粉机中进行磨粉；步骤3、素烧，得到素烧坯，备用；步骤4、施釉，对素烧坯进行施釉；步骤5、烧成，对施釉后的素烧坯进行烧成；本发明具有制作过程合理、光泽度好、釉料稳定无色块的优点。
The invention relates to firewood-fired porcelain yellow glaze. The firewood-fired porcelain yellow glazeis prepared from the following components in parts by weight: 20.18 parts of quartz, 33.23 parts of feldspar, 11.26 parts of calcite, 2.05 parts of talc, 18.83 parts of lime, 5.58 parts of phosphorus bone powder, 3.48 parts of agate stone, 2.56 parts of water bone stone and 2.83 parts of white metal soil; quartz sand is adopted as the quartz, the content of quartz in the quartz sand is greater than or equal to 90%; the feldspar is one or a combination of albite and potassium feldspar; and the phosphorus bone powder is any one of cattle bone powder, pig bone powder or horse bone powder, and the content of phosphorus is greater than or equal to 14.5%. The preparation method comprises the following steps of: step 1, green body preparation, specifically, preparing a green body for later use; step 2, grinding, specifically, weighing the components of the glaze according to the formula, and adding the materials into a Raymond mill for grinding; step 3, biscuit firing, specifically, performing biscuit firing to obtain a biscuit firing blank for use; step 4, glazing, specifically, glazing the biscuit firing blank; and step 5, firing, specifically, firing the glazed biscuit firing blank. The preparation process of the firewood-fired porcelain yellow glaze is reasonable, has good glossiness and is stable and free of color blocks.
本发明涉及柴瓷谷黄釉，它是由各组分按照以下重量配比制成：石英20.18份、长石33.23份、方解石11.26份、滑石2.05份、青灰18.83份、磷骨粉5.58份、玛瑙石3.48份、水骨石2.56份、乌金土2.83份，石英采用的是石英砂，石英砂中石英的含量≥90%，长石为钠长石和钾长石中的一种或两种的组合，磷骨粉为牛骨粉、猪骨粉或马骨粉中任意一种，其中磷的含量≥14.5%；它的制成包括以下步骤：步骤1、坯体制备：制备坯体备用；步骤2、磨粉，按配方称取釉料的各组分，通将物料加入到雷蒙磨粉机中进行磨粉；步骤3、素烧，得到素烧坯，备用；步骤4、施釉，对素烧坯进行施釉；步骤5、烧成，对施釉后的素烧坯进行烧成；本发明具有制作过程合理、光泽度好、釉料稳定无色块的优点。
Firewood-fired porcelain yellow glaze
柴瓷谷黄釉