Eine Plattform für die Wissenschaft: Bauingenieurwesen, Architektur und Urbanistik
Eine Plattform für die Wissenschaft: Bauingenieurwesen, Architektur und Urbanistik
The invention relates to the technical field of comprehensive utilization of solid waste liquid and waste, in particular to a comprehensive utilization method of desulfurized gypsum waste water. The method comprises the following steps: adding desulfurized gypsum wastewater and fly ash by using a pulping stirrer, stirring for a certain time, and heating the pulping temperature to a certain temperature by using steam after the measured slurry diffusivity reaches the standard; beating the prepared slurry into a pouring and stirring tank, adding RGM concrete reinforcing agent slurry, then adding lime and aluminum powder, uniformly stirring, and pouring the slurry into a mold box; moving the mold box where the slurry is poured to a static curing room for static gas generation; after standing gas generation is finished and a green body reaches the hardness for cutting, using a cutting machine for cutting; and putting the cut building block green body into a still kettle, and carrying out steam autoclaving at a certain pressure and temperature, so as to obtain an autoclaved aerated concrete building block finished product. The invention provides a method for utilizing solid waste liquid and waste water and comprehensively utilizing desulfurized gypsum waste water for producing the autoclaved aerated concrete building blocks.
本发明涉及固废液废综合利用技术领域，尤其涉及脱硫石膏废水的综合利用方法。包括以下步骤：使用制浆搅拌器，加入脱硫石膏废水、粉煤灰，搅拌一定时间，测量浆料扩散度达到标准后，使用蒸汽将制浆温度加热到一定温度；将制备好的浆料打到浇注搅拌罐内，加入RGM混凝土增强剂浆料，再加入白灰、铝粉，搅拌均匀后，将浆料浇注到模箱内；将已经浇注浆料的模箱移动到静养间静止发气；经过静养发气结束后，坯体达到具备切割的软硬度后，使用切割机切割；将切割后的砌块坯体放入蒸压釜内，通过一定压力和温度的蒸汽蒸压后，就可制出蒸压加气混凝土砌块成品。本发明提供出一种固废液废利用、生产蒸压加气混凝土砌块的脱硫石膏废水的综合利用方法。
The invention relates to the technical field of comprehensive utilization of solid waste liquid and waste, in particular to a comprehensive utilization method of desulfurized gypsum waste water. The method comprises the following steps: adding desulfurized gypsum wastewater and fly ash by using a pulping stirrer, stirring for a certain time, and heating the pulping temperature to a certain temperature by using steam after the measured slurry diffusivity reaches the standard; beating the prepared slurry into a pouring and stirring tank, adding RGM concrete reinforcing agent slurry, then adding lime and aluminum powder, uniformly stirring, and pouring the slurry into a mold box; moving the mold box where the slurry is poured to a static curing room for static gas generation; after standing gas generation is finished and a green body reaches the hardness for cutting, using a cutting machine for cutting; and putting the cut building block green body into a still kettle, and carrying out steam autoclaving at a certain pressure and temperature, so as to obtain an autoclaved aerated concrete building block finished product. The invention provides a method for utilizing solid waste liquid and waste water and comprehensively utilizing desulfurized gypsum waste water for producing the autoclaved aerated concrete building blocks.
本发明涉及固废液废综合利用技术领域，尤其涉及脱硫石膏废水的综合利用方法。包括以下步骤：使用制浆搅拌器，加入脱硫石膏废水、粉煤灰，搅拌一定时间，测量浆料扩散度达到标准后，使用蒸汽将制浆温度加热到一定温度；将制备好的浆料打到浇注搅拌罐内，加入RGM混凝土增强剂浆料，再加入白灰、铝粉，搅拌均匀后，将浆料浇注到模箱内；将已经浇注浆料的模箱移动到静养间静止发气；经过静养发气结束后，坯体达到具备切割的软硬度后，使用切割机切割；将切割后的砌块坯体放入蒸压釜内，通过一定压力和温度的蒸汽蒸压后，就可制出蒸压加气混凝土砌块成品。本发明提供出一种固废液废利用、生产蒸压加气混凝土砌块的脱硫石膏废水的综合利用方法。
Desulfurized gypsum comprehensive resource utilization formula and process
| Europäisches Patentamt | 2021
Method for preparing desulfurized gypsum from dry desulfurized ash
| Europäisches Patentamt | 2020