Resin concrete, preparation method of resin concrete, steel bridge deck pavement structure and construction method of steel bridge deck pavement structure
The invention provides resin concrete and a preparation method thereof, and a steel bridge deck pavement structure and a construction method thereof. The resin concrete is modified resin concrete based on a silane coupling agent, and comprises the following components in parts by mass: 0.1 to 3 parts of a curing agent, 10 to 30 parts of a modified resin binder, and 80 to 200 parts of aggregate, wherein the modified resin binder is a resin binder modified by a silane coupling agent. By adopting the technical scheme, the invention aims to provide the concrete which has good mechanical properties and low-temperature stability, so that different pavement requirements are met.
本发明提供了一种树脂混凝土及其制备方法、钢桥面铺装结构及其施工方法。其中，该树脂混凝土为基于硅烷偶联剂改性的树脂混凝土，该树脂混凝土包括：固化剂：0.1质量份至3质量份；改性树脂结合料：10质量份至30质量份；集料：80质量份至200质量份。其中，改性树脂结合料为经过硅烷偶联剂改性的树脂结合料。本发明采用上述技术方案旨在提供一种具有良好的力学性能并且同时兼顾低温稳定性的混凝土，从而适应不同的铺装需求。
Resin concrete, preparation method of resin concrete, steel bridge deck pavement structure and construction method of steel bridge deck pavement structure
The invention provides resin concrete and a preparation method thereof, and a steel bridge deck pavement structure and a construction method thereof. The resin concrete is modified resin concrete based on a silane coupling agent, and comprises the following components in parts by mass: 0.1 to 3 parts of a curing agent, 10 to 30 parts of a modified resin binder, and 80 to 200 parts of aggregate, wherein the modified resin binder is a resin binder modified by a silane coupling agent. By adopting the technical scheme, the invention aims to provide the concrete which has good mechanical properties and low-temperature stability, so that different pavement requirements are met.
本发明提供了一种树脂混凝土及其制备方法、钢桥面铺装结构及其施工方法。其中，该树脂混凝土为基于硅烷偶联剂改性的树脂混凝土，该树脂混凝土包括：固化剂：0.1质量份至3质量份；改性树脂结合料：10质量份至30质量份；集料：80质量份至200质量份。其中，改性树脂结合料为经过硅烷偶联剂改性的树脂结合料。本发明采用上述技术方案旨在提供一种具有良好的力学性能并且同时兼顾低温稳定性的混凝土，从而适应不同的铺装需求。
Resin concrete, preparation method of resin concrete, steel bridge deck pavement structure and construction method of steel bridge deck pavement structure
树脂混凝土及其制备方法、钢桥面铺装结构及其施工方法
19.11.2021
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2022
Composite resin concrete steel bridge deck pavement structure and construction method thereof
| Europäisches Patentamt | 2021
Composite resin concrete steel bridge deck pavement structure and construction method thereof
| Europäisches Patentamt | 2022
Concrete pavement structure for steel bridge deck and pavement method of concrete pavement structure
| Europäisches Patentamt | 2023
Steel-concrete combined bridge deck pavement structure and construction method
| Europäisches Patentamt | 2024