Lightweight high-performance boron carbide-based bulletproof ceramic and preparation method thereof
The invention discloses lightweight high-performance boron carbide-based bulletproof ceramic and a preparation method thereof. The lightweight high-performance boron carbide-based bulletproof ceramic is prepared from, by weight, 100 parts of boron carbide powder, 3-15 parts of multiphase additive powder, 50-60 parts of water, 0.1-1.5 parts of a dispersing agent and 2-5 parts of a binder, and gas the density of 97-99%, the bending strength of 420-500 MPa, the fracture toughness of 4.2-4.6 MPa.m<1/2>, and the Vickers hardness of 30-33 GPa. The preparation method comprises the steps of powder mixing, slurry preparation, spray granulation, blank pressing, sintering molding and sintered blank sand blasting treatment. According to the invention, the light high-performance boron carbide-based bulletproof ceramic with the smooth surface is obtained, the sintering activity of a boron carbide powder material is effectively improved, the sintering temperature is reduced, the cost of the sintering machining process is reduced, and the quality of mass production of products is stable.
本发明公开了一种轻质高性能碳化硼基防弹陶瓷及其制备方法，轻质高性能碳化硼基防弹陶瓷，按重量份数计，包括碳化硼粉体100份，复相添加剂粉体3‑15份，水50‑60份，分散剂0.1‑1.5份和粘结剂2‑5份；致密度为97‑99％，抗弯强度为420‑500MPa，断裂韧性为4.2‑4.6MPa·m1/2，维氏硬度为30‑33GPa。制备方法，包括步骤：粉体混合，浆料制备，喷雾造粒，压制毛坯，烧结成型，烧结坯喷砂处理，获得表面光滑的轻质高性能碳化硼基防弹陶瓷，有效提高碳化硼粉体材料的烧结活性及降低烧结温度，降低了烧结加工过程成本，产品大批量生产的质量稳定。
Lightweight high-performance boron carbide-based bulletproof ceramic and preparation method thereof
The invention discloses lightweight high-performance boron carbide-based bulletproof ceramic and a preparation method thereof. The lightweight high-performance boron carbide-based bulletproof ceramic is prepared from, by weight, 100 parts of boron carbide powder, 3-15 parts of multiphase additive powder, 50-60 parts of water, 0.1-1.5 parts of a dispersing agent and 2-5 parts of a binder, and gas the density of 97-99%, the bending strength of 420-500 MPa, the fracture toughness of 4.2-4.6 MPa.m<1/2>, and the Vickers hardness of 30-33 GPa. The preparation method comprises the steps of powder mixing, slurry preparation, spray granulation, blank pressing, sintering molding and sintered blank sand blasting treatment. According to the invention, the light high-performance boron carbide-based bulletproof ceramic with the smooth surface is obtained, the sintering activity of a boron carbide powder material is effectively improved, the sintering temperature is reduced, the cost of the sintering machining process is reduced, and the quality of mass production of products is stable.
本发明公开了一种轻质高性能碳化硼基防弹陶瓷及其制备方法，轻质高性能碳化硼基防弹陶瓷，按重量份数计，包括碳化硼粉体100份，复相添加剂粉体3‑15份，水50‑60份，分散剂0.1‑1.5份和粘结剂2‑5份；致密度为97‑99％，抗弯强度为420‑500MPa，断裂韧性为4.2‑4.6MPa·m1/2，维氏硬度为30‑33GPa。制备方法，包括步骤：粉体混合，浆料制备，喷雾造粒，压制毛坯，烧结成型，烧结坯喷砂处理，获得表面光滑的轻质高性能碳化硼基防弹陶瓷，有效提高碳化硼粉体材料的烧结活性及降低烧结温度，降低了烧结加工过程成本，产品大批量生产的质量稳定。
Lightweight high-performance boron carbide-based bulletproof ceramic and preparation method thereof
一种轻质高性能碳化硼基防弹陶瓷及其制备方法
ZHAO GUOZHANG (Autor:in) / WANG HONGTAO (Autor:in) / XIE MING (Autor:in)
19.11.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Lightweight bulletproof boron carbide material and preparation method thereof
| Europäisches Patentamt | 2021
Pressureless sintered boron carbide bulletproof ceramic and preparation method thereof
| Europäisches Patentamt | 2021
Boron carbide bulletproof ceramic with radar stealth performance and preparation method thereof
| Europäisches Patentamt | 2022
Preparation method of bulletproof boron carbide composite ceramic
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2024