Anti-erosion calcium aluminate castable
The invention relates to an anti-erosion calcium aluminate castable. The calcium aluminate castable is prepared from the following components in percentage by weight: 65 to 69.9 percent of a mixture of calcium aluminate aggregate and fine powder, 10 to 13 percent of aluminum oxide hollow spheres, 2 to 10 percent of pure aluminate cement, 5 to 11 percent of aluminum oxide micro powder, 0.5 to 3 percent of an additive and 0.1 percent of a high-efficiency dispersing agent, the sum of the weight of the components is 100%. The calcium aluminate castable disclosed by the invention is high in construction speed, low in volume density and high in steel slag and molten steel erosion resistance, and plays roles in energy conservation, emission reduction, safety guarantee and the like.
一种抗侵蚀的铝酸钙浇注料，所述的铝酸钙浇注料的各组分的重量百分比为：铝酸钙骨料和细粉的混合物：65‑69.9％，氧化铝空心球占比为10‑13％，纯铝酸盐水泥占比为2‑10％，氧化铝微粉占比为5‑11％，添加剂为0.5‑3％，高效分散剂为0.1％；以上各组分的组配重量之和为100％；本发明的铝酸钙浇注料不仅施工速度快，体积密度也低，抗钢渣和钢水的侵蚀能力也强，起到了节能减排，保安全等方面的作用。
Anti-erosion calcium aluminate castable
The invention relates to an anti-erosion calcium aluminate castable. The calcium aluminate castable is prepared from the following components in percentage by weight: 65 to 69.9 percent of a mixture of calcium aluminate aggregate and fine powder, 10 to 13 percent of aluminum oxide hollow spheres, 2 to 10 percent of pure aluminate cement, 5 to 11 percent of aluminum oxide micro powder, 0.5 to 3 percent of an additive and 0.1 percent of a high-efficiency dispersing agent, the sum of the weight of the components is 100%. The calcium aluminate castable disclosed by the invention is high in construction speed, low in volume density and high in steel slag and molten steel erosion resistance, and plays roles in energy conservation, emission reduction, safety guarantee and the like.
一种抗侵蚀的铝酸钙浇注料，所述的铝酸钙浇注料的各组分的重量百分比为：铝酸钙骨料和细粉的混合物：65‑69.9％，氧化铝空心球占比为10‑13％，纯铝酸盐水泥占比为2‑10％，氧化铝微粉占比为5‑11％，添加剂为0.5‑3％，高效分散剂为0.1％；以上各组分的组配重量之和为100％；本发明的铝酸钙浇注料不仅施工速度快，体积密度也低，抗钢渣和钢水的侵蚀能力也强，起到了节能减排，保安全等方面的作用。
Anti-erosion calcium aluminate castable
一种抗侵蚀的铝酸钙浇注料
BAI HONGYU (Autor:in) / WANG GUOLIN (Autor:in) / BAI ZHONGSHUAN (Autor:in)
26.11.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Calcium aluminate cements for emerging castable technology
| Tema Archiv | 1985
Calcium aluminate cement-combined corundum castable and preparation method thereof
| Europäisches Patentamt | 2015
Calcium aluminate based refractory castable and application thereof to casting production
| Europäisches Patentamt | 2015