SiO2 phase-change temperature-control microcapsule modified cement building material as well as preparation method and application thereof
The invention relates to a SiO2 phase-change temperature-control microcapsule modified cement building material as well as a preparation method and application thereof, and belongs to the technical field of building heat preservation. The cement building material is prepared from the following raw materials in parts by weight: 1 part of cement, 0.9-2 parts of sand, 0-3 parts of stones, 0.4-1.1 parts of water, 0.003-0.025 parts of a water reducing agent and 0.05-0.25 parts of SiO2 phase-change temperature-control microcapsules. According to the SiO2 phase-change temperature-control microcapsule modified cement building material, the temperature of a wall body can be controlled and adjusted by adding the novel energy-saving and environment-friendly phase-change microcapsules with SiO2 as a shell material. The addition of the phase-change microcapsules can enable the wall to have a good control effect on the temperature.
本发明涉及一种SiO2相变控温微胶囊改性水泥建材及其制备方法和应用，属于建筑保温技术领域。该水泥建材包括以下重量份的原料：水泥1份，沙子0.9‑2份，石子0‑3份，水0.4‑1.1份，减水剂0.003‑0.025份，SiO2相变控温微胶囊0.05‑0.25份。上述SiO2相变控温微胶囊改性水泥建材，通过添加新型节能环保型SiO2为壳材的相变微胶囊对墙体温度进行控温调节。该相变微胶囊的加入可以使墙体对温度有一个良好的控制效果。
SiO2 phase-change temperature-control microcapsule modified cement building material as well as preparation method and application thereof
The invention relates to a SiO2 phase-change temperature-control microcapsule modified cement building material as well as a preparation method and application thereof, and belongs to the technical field of building heat preservation. The cement building material is prepared from the following raw materials in parts by weight: 1 part of cement, 0.9-2 parts of sand, 0-3 parts of stones, 0.4-1.1 parts of water, 0.003-0.025 parts of a water reducing agent and 0.05-0.25 parts of SiO2 phase-change temperature-control microcapsules. According to the SiO2 phase-change temperature-control microcapsule modified cement building material, the temperature of a wall body can be controlled and adjusted by adding the novel energy-saving and environment-friendly phase-change microcapsules with SiO2 as a shell material. The addition of the phase-change microcapsules can enable the wall to have a good control effect on the temperature.
本发明涉及一种SiO2相变控温微胶囊改性水泥建材及其制备方法和应用，属于建筑保温技术领域。该水泥建材包括以下重量份的原料：水泥1份，沙子0.9‑2份，石子0‑3份，水0.4‑1.1份，减水剂0.003‑0.025份，SiO2相变控温微胶囊0.05‑0.25份。上述SiO2相变控温微胶囊改性水泥建材，通过添加新型节能环保型SiO2为壳材的相变微胶囊对墙体温度进行控温调节。该相变微胶囊的加入可以使墙体对温度有一个良好的控制效果。
SiO2 phase-change temperature-control microcapsule modified cement building material as well as preparation method and application thereof
SiO2相变控温微胶囊改性水泥建材及其制备方法和应用
YANG JINGLEI (Autor:in) / SHEN ZHAOBO (Autor:in) / AN JINLIANG (Autor:in) / TANG ZHENZHONG (Autor:in) / LIU XIAOLI (Autor:in) / CHEN YANCHAO (Autor:in)
17.12.2021
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2023
Cement paste temperature control self-repairing microcapsule and preparation method thereof
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2022