Preparation method of fireproof and waterproof floor
The invention discloses a preparation method of a fireproof and waterproof floor, which comprises the following steps: sequentially carrying out one-time hot press molding on melamine paper, a high-density fiberboard and balance paper from top to bottom at the hot press temperature of 190-210 DEG C under the pressure of 3-5 MPa for 30-40 seconds; static curing is conducted, specifically, the hot-pressed floor is placed at the room temperature to be cured for 7-10 d, and then grooving, beveling and edge sealing are conducted; finally, finished products are inspected, packaged and warehoused. The fireproof and waterproof high-density fiberboard is adopted as a base material, the fireproof performance of a wallboard main body component is guaranteed, in addition, melamine paper and balance paper are selected as the surface decoration layer and the back balance layer, the thickness of the melamine paper and the balance paper is only 0.1-0.2 mm, the A-level fireproof requirement can be completely met, and compared with a common laminate floor plastic floor, the fireproof and waterproof wallboard has the advantages that the fireproof performance is good, and the fireproof performance is good. The floor can reach the national standard A-level fireproof performance.
本发明公开了一种防火防水地板的制备方法，将三聚氰胺纸、高密度纤维板、平衡纸从上到下的顺序一次热压成型，热压温度190‑210℃，压力3‑5MPa，热压时间30‑40秒；静止养护，将热压的地板置于室温下养护7‑10d后开槽，倒边、封边；最后成品检验、包装入库。本发明采用防火防水高密度纤维板作为基材，保证了墙板主体成份的防火性能，另外选用三聚氰胺纸和平衡纸作为表面装饰层和背面平衡层，两者厚度薄，其厚度仅为0.1‑0.2mm，完全能满足A级防火的要求，相对与普通强化地板塑胶地板，该地板可达到国标A级防火性能。
Preparation method of fireproof and waterproof floor
The invention discloses a preparation method of a fireproof and waterproof floor, which comprises the following steps: sequentially carrying out one-time hot press molding on melamine paper, a high-density fiberboard and balance paper from top to bottom at the hot press temperature of 190-210 DEG C under the pressure of 3-5 MPa for 30-40 seconds; static curing is conducted, specifically, the hot-pressed floor is placed at the room temperature to be cured for 7-10 d, and then grooving, beveling and edge sealing are conducted; finally, finished products are inspected, packaged and warehoused. The fireproof and waterproof high-density fiberboard is adopted as a base material, the fireproof performance of a wallboard main body component is guaranteed, in addition, melamine paper and balance paper are selected as the surface decoration layer and the back balance layer, the thickness of the melamine paper and the balance paper is only 0.1-0.2 mm, the A-level fireproof requirement can be completely met, and compared with a common laminate floor plastic floor, the fireproof and waterproof wallboard has the advantages that the fireproof performance is good, and the fireproof performance is good. The floor can reach the national standard A-level fireproof performance.
本发明公开了一种防火防水地板的制备方法，将三聚氰胺纸、高密度纤维板、平衡纸从上到下的顺序一次热压成型，热压温度190‑210℃，压力3‑5MPa，热压时间30‑40秒；静止养护，将热压的地板置于室温下养护7‑10d后开槽，倒边、封边；最后成品检验、包装入库。本发明采用防火防水高密度纤维板作为基材，保证了墙板主体成份的防火性能，另外选用三聚氰胺纸和平衡纸作为表面装饰层和背面平衡层，两者厚度薄，其厚度仅为0.1‑0.2mm，完全能满足A级防火的要求，相对与普通强化地板塑胶地板，该地板可达到国标A级防火性能。
Preparation method of fireproof and waterproof floor
一种防火防水地板的制备方法
WEI YUKANG (Autor:in) / NI QINGLAN (Autor:in) / DONG YUJIAO (Autor:in) / LU WEI (Autor:in) / LI JIN (Autor:in)
08.03.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
B32B
LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
,
Schichtkörper, d.h. aus Ebenen oder gewölbten Schichten, z.B. mit zell- oder wabenförmiger Form, aufgebaute Erzeugnisse
/
E04F
FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
,
Ausbau von Bauwerken, z.B. Treppen, Fußböden
Fireproof and waterproof biomass floor and preparation method thereof
| Europäisches Patentamt | 2020
Fireproof and waterproof biomass floor and preparation method thereof
| Europäisches Patentamt | 2020