Preparation method of dolomite composite material
The invention provides a preparation method of a dolomite composite material. The preparation method of the dolomite composite material comprises the following steps: S1, preparing raw materials: (1) preparing dolomite, a dispersing agent, zirconium oxide powder and water glass liquid; s2, a manufacturing process: (1) taking 300g of dolomite, putting the dolomite into a crusher, crushing, and then filtering through a filter screen to finally obtain dolomite powder with the granularity of 0.40-40.15 mu m; (2) pouring the crushed dolomite powder into disc type stirring mill equipment, and then adding water glass liquid and a dispersing agent according to a certain proportion; the preparation method of the dolomite composite material provided by the invention has the advantages that the thermal insulation performance of the lining pipe is effectively improved on the basis of not influencing the pressure transmission performance of the dolomite, so that the production capacity can be increased, the consumption can be reduced, and the energy-saving and synergistic production can be realized.
本发明提供一种白云石复合材料的制备方法。所述白云石复合材料的制备方法包括以下步骤：S1、准备原料：(1).白云石、分散剂、氧化锆粉和水玻璃液体；S2、制作工序：(1).取300g的白云石放置到粉碎机内进行粉碎，然后通过过滤网进行过滤，最后来得到白云石粉，所述白云石粉的颗粒度为0.40‑40.15μm；(2).将上述粉碎好的白云石粉倒入到盘式搅拌磨设备中，然后按照一定的比例加入水玻璃液体和分散剂。本发明提供的白云石复合材料的制备方法具有在不影响白云石传压性能的基础上，有效增加了内衬管的保温性能，致使可以达到增加产能，降低消耗，实现节能和增效生产的优点。
Preparation method of dolomite composite material
The invention provides a preparation method of a dolomite composite material. The preparation method of the dolomite composite material comprises the following steps: S1, preparing raw materials: (1) preparing dolomite, a dispersing agent, zirconium oxide powder and water glass liquid; s2, a manufacturing process: (1) taking 300g of dolomite, putting the dolomite into a crusher, crushing, and then filtering through a filter screen to finally obtain dolomite powder with the granularity of 0.40-40.15 mu m; (2) pouring the crushed dolomite powder into disc type stirring mill equipment, and then adding water glass liquid and a dispersing agent according to a certain proportion; the preparation method of the dolomite composite material provided by the invention has the advantages that the thermal insulation performance of the lining pipe is effectively improved on the basis of not influencing the pressure transmission performance of the dolomite, so that the production capacity can be increased, the consumption can be reduced, and the energy-saving and synergistic production can be realized.
本发明提供一种白云石复合材料的制备方法。所述白云石复合材料的制备方法包括以下步骤：S1、准备原料：(1).白云石、分散剂、氧化锆粉和水玻璃液体；S2、制作工序：(1).取300g的白云石放置到粉碎机内进行粉碎，然后通过过滤网进行过滤，最后来得到白云石粉，所述白云石粉的颗粒度为0.40‑40.15μm；(2).将上述粉碎好的白云石粉倒入到盘式搅拌磨设备中，然后按照一定的比例加入水玻璃液体和分散剂。本发明提供的白云石复合材料的制备方法具有在不影响白云石传压性能的基础上，有效增加了内衬管的保温性能，致使可以达到增加产能，降低消耗，实现节能和增效生产的优点。
Preparation method of dolomite composite material
一种白云石复合材料的制备方法
LIU HONGWEI (Autor:in) / ZHANG XIANGFA (Autor:in) / WEI XING (Autor:in) / WANG YONGKAI (Autor:in) / WANG DAPENG (Autor:in) / JIA SHUAIZHONG (Autor:in) / ZHAI GANGLEI (Autor:in)
10.05.2022
Patent
Elektronische Ressource
Chinesisch
Dolomite lining composite material and preparation method thereof
| Europäisches Patentamt | 2024