High-temperature-resistant non-stick ceramic pot and preparation method thereof
The invention relates to the field of ceramic products, in particular to a high-temperature-resistant non-stick ceramic pot and a preparation method thereof.The ground coat is prepared from, by weight, 55-65 parts of aluminum ash stone, 10-14 parts of kaolin, 13-16 parts of quartz, 13-16 parts of limestone, 1-3 parts of barium carbonate, 30-34 parts of bones, 50-54 parts of wollastonite and 80-84 parts of pigment; the cover glaze is prepared from the following raw material components in parts by weight: 58 to 62 parts of aluminum ash stone, 10 to 14 parts of kaolin, 13 to 15 parts of quartz, 14 to 16 parts of limestone, 1 to 3 parts of barium carbonate, 30 to 34 parts of bone, 50 to 54 parts of wollastonite, 80 to 84 parts of pigment and 1 to 3 parts of cohesive soil. Through a double-layer glazing mode, the fineness of the raw materials of the cover glaze is improved to 600 meshes, and clay is added, so that the glaze surface has few cracks in a microscopic state, the flatness of the glaze surface is high, and the adhesion resistance is good; blank glaze expansion coefficients are similar, the blank glaze adaptability is good, and the thermal stability is good.
本发明涉及陶瓷制品领域，具体涉及一种耐高温不粘陶瓷锅及其制备方法，底釉的原料以重量份计，包括如下组分：铝灰石55‑65份，高岭土10‑14份，石英13‑16份，石灰石13‑16份，碳酸钡1‑3份，骨头30‑34份，硅灰石50‑54份，色料80‑84份；所述面釉的原料以重量份计，包括如下组分：铝灰石58‑62份，高岭土10‑14份，石英13‑15份，石灰石14‑16份，碳酸钡1‑3份，骨头30‑34份，硅灰石50‑54份，色料80‑84份，粘性土1‑3份。通过双层上釉的方式，面釉的原料细度提升至600目，并添加黏土，釉面显微状态下裂纹少、釉面平整度高，抗粘性好；坯釉膨胀系数相近，坯釉适应性好，热稳定性好。
High-temperature-resistant non-stick ceramic pot and preparation method thereof
The invention relates to the field of ceramic products, in particular to a high-temperature-resistant non-stick ceramic pot and a preparation method thereof.The ground coat is prepared from, by weight, 55-65 parts of aluminum ash stone, 10-14 parts of kaolin, 13-16 parts of quartz, 13-16 parts of limestone, 1-3 parts of barium carbonate, 30-34 parts of bones, 50-54 parts of wollastonite and 80-84 parts of pigment; the cover glaze is prepared from the following raw material components in parts by weight: 58 to 62 parts of aluminum ash stone, 10 to 14 parts of kaolin, 13 to 15 parts of quartz, 14 to 16 parts of limestone, 1 to 3 parts of barium carbonate, 30 to 34 parts of bone, 50 to 54 parts of wollastonite, 80 to 84 parts of pigment and 1 to 3 parts of cohesive soil. Through a double-layer glazing mode, the fineness of the raw materials of the cover glaze is improved to 600 meshes, and clay is added, so that the glaze surface has few cracks in a microscopic state, the flatness of the glaze surface is high, and the adhesion resistance is good; blank glaze expansion coefficients are similar, the blank glaze adaptability is good, and the thermal stability is good.
本发明涉及陶瓷制品领域，具体涉及一种耐高温不粘陶瓷锅及其制备方法，底釉的原料以重量份计，包括如下组分：铝灰石55‑65份，高岭土10‑14份，石英13‑16份，石灰石13‑16份，碳酸钡1‑3份，骨头30‑34份，硅灰石50‑54份，色料80‑84份；所述面釉的原料以重量份计，包括如下组分：铝灰石58‑62份，高岭土10‑14份，石英13‑15份，石灰石14‑16份，碳酸钡1‑3份，骨头30‑34份，硅灰石50‑54份，色料80‑84份，粘性土1‑3份。通过双层上釉的方式，面釉的原料细度提升至600目，并添加黏土，釉面显微状态下裂纹少、釉面平整度高，抗粘性好；坯釉膨胀系数相近，坯釉适应性好，热稳定性好。
High-temperature-resistant non-stick ceramic pot and preparation method thereof
耐高温不粘陶瓷锅及其制备方法
TU JIANBANG (Autor:in)
10.06.2022
Patent
Elektronische Ressource
Chinesisch
Non-stick heat-resistant ceramic pot glaze and preparation method thereof
| Europäisches Patentamt | 2021
High-temperature-resistant ceramic and preparation method thereof
| Europäisches Patentamt | 2020
Ceramic ware for Non-stick and heat-resistant frying pan and preparation method thereof
Europäisches Patentamt | 2023
Ceramic ware for Non-stick and heat-resistant frying pan and preparation method thereof
| Europäisches Patentamt | 2022
High-temperature-resistant radiation-resistant piezoelectric ceramic and preparation method thereof
| Europäisches Patentamt | 2021