Preparation method of high-white daily blank mud
The invention discloses a production method of high-white-day blank mud, which comprises the following steps: step 1, adding raw materials of the high-white-day blank mud into a pulverizer, and pulverizing to obtain blank mud powder; step 2, screening the crushed blank mud powder to remove particulate matters in the blank mud powder, then pouring the screened blank mud powder into a stirring tank filled with a mineral bleaching agent, stirring for 10-20 hours at the temperature of 60-80 DEG C, filtering and drying to obtain a bleached blank mud raw material; step 3, putting the blank mud raw material into a ball milling tank, grinding for 32-42 hours, discharging and discharging slurry; the preparation method comprises the following steps: washing and whitening a blank mud raw material by using a mineral bleaching agent, then carrying out magnetic separation, screening and aging on the blank mud raw material, and finally carrying out filter pressing and dehydration to form a blank mud cake, thereby obtaining the high-whiteness daily blank mud, and the blank mud raw material is rinsed and whitened by using the mineral bleaching agent, so that the whiteness of the blank mud is greatly improved.
本发明公开了一种高白日用坯泥的制作方法，包括以下步骤:步骤1：将高白日用坯泥原料加入到磨粉机中进入粉碎，得到坯泥粉末；步骤2：对粉碎后的坯泥粉末进行筛选，除去坯泥粉末中的颗粒物，然后将筛选后的坯泥粉末倒入盛有入矿物漂白剂的搅拌罐中，并在温度60‑80℃条件下，搅拌10‑20h后，过滤干燥，得到漂白后的坯泥原料；步骤3：将坯泥原料投入到球磨罐，经32‑42h研磨，卸料出浆；然后对坯泥原料进行磁选、筛分、陈腐，最后压滤脱水成坯泥泥饼，即得到高白日用坯泥，本发明通过矿物漂白剂对坯泥原料进行漂洗增白，其将大大提高坯泥的白度。
Preparation method of high-white daily blank mud
The invention discloses a production method of high-white-day blank mud, which comprises the following steps: step 1, adding raw materials of the high-white-day blank mud into a pulverizer, and pulverizing to obtain blank mud powder; step 2, screening the crushed blank mud powder to remove particulate matters in the blank mud powder, then pouring the screened blank mud powder into a stirring tank filled with a mineral bleaching agent, stirring for 10-20 hours at the temperature of 60-80 DEG C, filtering and drying to obtain a bleached blank mud raw material; step 3, putting the blank mud raw material into a ball milling tank, grinding for 32-42 hours, discharging and discharging slurry; the preparation method comprises the following steps: washing and whitening a blank mud raw material by using a mineral bleaching agent, then carrying out magnetic separation, screening and aging on the blank mud raw material, and finally carrying out filter pressing and dehydration to form a blank mud cake, thereby obtaining the high-whiteness daily blank mud, and the blank mud raw material is rinsed and whitened by using the mineral bleaching agent, so that the whiteness of the blank mud is greatly improved.
本发明公开了一种高白日用坯泥的制作方法，包括以下步骤:步骤1：将高白日用坯泥原料加入到磨粉机中进入粉碎，得到坯泥粉末；步骤2：对粉碎后的坯泥粉末进行筛选，除去坯泥粉末中的颗粒物，然后将筛选后的坯泥粉末倒入盛有入矿物漂白剂的搅拌罐中，并在温度60‑80℃条件下，搅拌10‑20h后，过滤干燥，得到漂白后的坯泥原料；步骤3：将坯泥原料投入到球磨罐，经32‑42h研磨，卸料出浆；然后对坯泥原料进行磁选、筛分、陈腐，最后压滤脱水成坯泥泥饼，即得到高白日用坯泥，本发明通过矿物漂白剂对坯泥原料进行漂洗增白，其将大大提高坯泥的白度。
Preparation method of high-white daily blank mud
一种高白日用坯泥的制作方法
PAN JUNMING (Autor:in) / LIAO ZHIJIAN (Autor:in) / LU RIGAO (Autor:in) / GUO RENHU (Autor:in)
24.06.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Crystal white porcelain blank and preparation method thereof
| Europäisches Patentamt | 2023
Blank for preparing patting nixing pottery and preparation method of blank
| Europäisches Patentamt | 2015
High white eco-friendly degraded blank soil and making technology thereof
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2023