Firing method of porcelain with peony lines
The invention discloses a method for firing porcelain with peony lines. The method comprises the following steps: selecting pug; selecting glaze; forming a green body; grooving the lines; the glaze is repeatedly applied, and the glaze at the groove is 0.5-0.8 cm thicker than the surrounding part; the kiln temperature is controlled at 1260 DEG C; it is guaranteed that the fired carcass is taken out of a kiln at the temperature of about 200 DEG C and then rapidly cooled to 10 DEG C, so that the expansion coefficient and the shrinkage coefficient are different, the glaze cracking effect is generated, and the desired cracking lines are achieved. The invention belongs to the technical field of porcelain preparation, and particularly provides a method for firing peony grain porcelain, which is simple to operate, low in cost and convenient to process, and controls the diversity and attractiveness of opening by controlling the thickness of a groove and glaze.
本发明公开了一种牡丹纹纹路瓷器的烧制方法，包括泥料选择；釉料选择；坯体成型；纹路开槽；重复施釉，凹槽处的釉料比周围部位厚0.5‑0.8cm；烧窑温度控制在1260℃；保证烧制的胎体在200℃左右拿出窑炉，然后对其急速降温至10℃，使膨胀和收缩系数不一样，产生釉面开片的效果，从而达到想要的开片纹路。本发明属于瓷器制备技术领域，具体是提供了一种操作简单，成本低，且加工方便，通过控制凹槽与釉的厚薄，从而控制开纹的多样化与美观性的牡丹纹纹路瓷器的烧制方法。
Firing method of porcelain with peony lines
The invention discloses a method for firing porcelain with peony lines. The method comprises the following steps: selecting pug; selecting glaze; forming a green body; grooving the lines; the glaze is repeatedly applied, and the glaze at the groove is 0.5-0.8 cm thicker than the surrounding part; the kiln temperature is controlled at 1260 DEG C; it is guaranteed that the fired carcass is taken out of a kiln at the temperature of about 200 DEG C and then rapidly cooled to 10 DEG C, so that the expansion coefficient and the shrinkage coefficient are different, the glaze cracking effect is generated, and the desired cracking lines are achieved. The invention belongs to the technical field of porcelain preparation, and particularly provides a method for firing peony grain porcelain, which is simple to operate, low in cost and convenient to process, and controls the diversity and attractiveness of opening by controlling the thickness of a groove and glaze.
本发明公开了一种牡丹纹纹路瓷器的烧制方法，包括泥料选择；釉料选择；坯体成型；纹路开槽；重复施釉，凹槽处的釉料比周围部位厚0.5‑0.8cm；烧窑温度控制在1260℃；保证烧制的胎体在200℃左右拿出窑炉，然后对其急速降温至10℃，使膨胀和收缩系数不一样，产生釉面开片的效果，从而达到想要的开片纹路。本发明属于瓷器制备技术领域，具体是提供了一种操作简单，成本低，且加工方便，通过控制凹槽与釉的厚薄，从而控制开纹的多样化与美观性的牡丹纹纹路瓷器的烧制方法。
Firing method of porcelain with peony lines
一种牡丹纹纹路瓷器的烧制方法
LIU XIAODONG (Autor:in)
15.07.2022
Patent
Elektronische Ressource
Chinesisch
Manufacturing method of peony porcelain with uniformly distributed colors
| Europäisches Patentamt | 2024
Method for manufacturing peony porcelain based on overglaze color
| Europäisches Patentamt | 2024