Super-thick whole-body natural stone water permeable plate and preparation method thereof
The invention belongs to the field of permeable plates, and particularly relates to a super-thick whole-body natural stone permeable plate and a preparation method thereof. The thickness of the water-permeable plate is greater than 60mm, and the water-permeable plate is formed by firing a mixture consisting of a binder, a fluxing agent and aggregate, in the mixture, the mass percentage of the binder is 4-10%, the mass percentage of the fluxing agent is 2-6%, and the balance is the aggregate; the aggregate is composed of waste ceramic tile particles and granite tailing slag colored stone particles according to the mass ratio of (1-2): (2-1), and the aggregate adopts different particle size grading to form a permeable structure. According to the super-thick whole-body natural stone water permeable plate, the granite imitation state is integrally achieved from inside to outside, and the pursuit of people for the natural and heavy beauty of granite is more naturally explained; in addition, the water-permeable plate has higher bearing capacity, the durability of application is improved, and the application range of the water-permeable plate is widened.
本发明属于透水板领域，具体涉及一种超厚通体自然石透水板及其制备方法。该透水板的厚度大于60mm，由粘结剂、助熔剂和骨料组成的混合料烧制而成；混合料中，粘结剂的质量百分占比为4～10％，助熔剂的质量百分占比为2～6％，其余为骨料；所述骨料由废瓷砖颗粒和花岗岩尾矿渣彩石颗粒按质量比(1～2)：(2～1)组成，所述骨料采用不同粒径级配形成透水结构。本发明的超厚通体自然石透水板，由里到外一体式达到仿花岗岩状态，更自然地诠释了人们对花岗岩天然、厚重之美的追求；该透水板还具有更高的承载能力，提高了应用的耐久性，拓宽了透水板的应用范围。
Super-thick whole-body natural stone water permeable plate and preparation method thereof
The invention belongs to the field of permeable plates, and particularly relates to a super-thick whole-body natural stone permeable plate and a preparation method thereof. The thickness of the water-permeable plate is greater than 60mm, and the water-permeable plate is formed by firing a mixture consisting of a binder, a fluxing agent and aggregate, in the mixture, the mass percentage of the binder is 4-10%, the mass percentage of the fluxing agent is 2-6%, and the balance is the aggregate; the aggregate is composed of waste ceramic tile particles and granite tailing slag colored stone particles according to the mass ratio of (1-2): (2-1), and the aggregate adopts different particle size grading to form a permeable structure. According to the super-thick whole-body natural stone water permeable plate, the granite imitation state is integrally achieved from inside to outside, and the pursuit of people for the natural and heavy beauty of granite is more naturally explained; in addition, the water-permeable plate has higher bearing capacity, the durability of application is improved, and the application range of the water-permeable plate is widened.
本发明属于透水板领域，具体涉及一种超厚通体自然石透水板及其制备方法。该透水板的厚度大于60mm，由粘结剂、助熔剂和骨料组成的混合料烧制而成；混合料中，粘结剂的质量百分占比为4～10％，助熔剂的质量百分占比为2～6％，其余为骨料；所述骨料由废瓷砖颗粒和花岗岩尾矿渣彩石颗粒按质量比(1～2)：(2～1)组成，所述骨料采用不同粒径级配形成透水结构。本发明的超厚通体自然石透水板，由里到外一体式达到仿花岗岩状态，更自然地诠释了人们对花岗岩天然、厚重之美的追求；该透水板还具有更高的承载能力，提高了应用的耐久性，拓宽了透水板的应用范围。
Super-thick whole-body natural stone water permeable plate and preparation method thereof
一种超厚通体自然石透水板及其制备方法
CHEN WEIYOU (Autor:in) / FAN JING (Autor:in) / SHA QINGZHONG (Autor:in)
02.09.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Natural stone imitated stain-resistant water permeable brick and preparation method thereof
| Europäisches Patentamt | 2021
Stone imitating water permeable brick and preparation method thereof
| Europäisches Patentamt | 2020
Stone-like water permeable brick and preparation method thereof
| Europäisches Patentamt | 2020
Natural colored water-permeable adhesive stone pavement material and preparation process thereof
| Europäisches Patentamt | 2022