Ceramic tile adhesive and preparation method thereof
The invention provides a ceramic tile adhesive and a preparation method thereof, and relates to the technical field of adhesives. The tile glue comprises the following raw materials in parts by weight: 10-15 parts of reclaimed sand, 10-15 parts of cellulose ether, 5-10 parts of Portland cement, 5-10 parts of silica fume, 5-8 parts of sodium silicate, 5-10 parts of polymer modified cement mortar, 3-5 parts of fly ash, 1-3 parts of calcium formate, 2-5 parts of granulated blast furnace slag powder, 0.5-2 parts of an adhesive and 10-15 parts of clear water, and the fineness of the reclaimed sand is 0.45-0.55 mm; the ceramic tile adhesive further comprises one or more of a water-retaining agent, a defoaming agent and gypsum. The special cement mortar modified by high-quality polymer is applied in the preparation process, so that the produced ceramic tile adhesive finished product has high binding power and does not need to soak bricks and wet walls in construction, and meanwhile, a proper amount of defoaming agent, water-retaining agent or gypsum component is added, so that each tensile bonding strength of the ceramic tile adhesive is improved, and the ceramic tile adhesive has excellent weather resistance and impact resistance.
本发明提供一种瓷砖胶及其制备方法，涉及胶黏剂技术领域。该瓷砖胶，包括以下重量份的原料：再生砂10～15份、纤维素醚10～15份、硅酸盐水泥5～10份、硅灰5～10份、硅酸钠5～8份、聚合物改性水泥砂浆5～10份、粉煤灰3～5份、甲酸钙1～3份、粒化高炉矿渣粉2～5份、胶粘剂0.5～2份和清水10～15份，所述再生砂的细度为0.45～0.55mm；所述瓷砖胶还包括保水剂、消泡剂和生石膏中的一种或多种。通过在制备过程中应用优质聚合物改性特制水泥砂浆，使生产出的瓷砖胶成品具备高粘结力，施工中不用浸砖湿墙，同时通过添加适量的消泡剂、保水剂或生石膏成分，提高了瓷砖胶各项拉伸粘结强度，使瓷砖胶具有优良的耐候抗冲击性能。
Ceramic tile adhesive and preparation method thereof
The invention provides a ceramic tile adhesive and a preparation method thereof, and relates to the technical field of adhesives. The tile glue comprises the following raw materials in parts by weight: 10-15 parts of reclaimed sand, 10-15 parts of cellulose ether, 5-10 parts of Portland cement, 5-10 parts of silica fume, 5-8 parts of sodium silicate, 5-10 parts of polymer modified cement mortar, 3-5 parts of fly ash, 1-3 parts of calcium formate, 2-5 parts of granulated blast furnace slag powder, 0.5-2 parts of an adhesive and 10-15 parts of clear water, and the fineness of the reclaimed sand is 0.45-0.55 mm; the ceramic tile adhesive further comprises one or more of a water-retaining agent, a defoaming agent and gypsum. The special cement mortar modified by high-quality polymer is applied in the preparation process, so that the produced ceramic tile adhesive finished product has high binding power and does not need to soak bricks and wet walls in construction, and meanwhile, a proper amount of defoaming agent, water-retaining agent or gypsum component is added, so that each tensile bonding strength of the ceramic tile adhesive is improved, and the ceramic tile adhesive has excellent weather resistance and impact resistance.
本发明提供一种瓷砖胶及其制备方法，涉及胶黏剂技术领域。该瓷砖胶，包括以下重量份的原料：再生砂10～15份、纤维素醚10～15份、硅酸盐水泥5～10份、硅灰5～10份、硅酸钠5～8份、聚合物改性水泥砂浆5～10份、粉煤灰3～5份、甲酸钙1～3份、粒化高炉矿渣粉2～5份、胶粘剂0.5～2份和清水10～15份，所述再生砂的细度为0.45～0.55mm；所述瓷砖胶还包括保水剂、消泡剂和生石膏中的一种或多种。通过在制备过程中应用优质聚合物改性特制水泥砂浆，使生产出的瓷砖胶成品具备高粘结力，施工中不用浸砖湿墙，同时通过添加适量的消泡剂、保水剂或生石膏成分，提高了瓷砖胶各项拉伸粘结强度，使瓷砖胶具有优良的耐候抗冲击性能。
Ceramic tile adhesive and preparation method thereof
一种瓷砖胶及其制备方法