Combination formula of Hupu white mud and Qinzhou Nixing pottery clay and preparation process thereof
The invention provides a combined formula of Hupu white mud and Qinzhou Nixing pottery clay and a preparation process of the combined formula, and relates to the technical field of ceramic blank production. The Huupu white mud and Qinzhou Nixing pottery clay combined formula and the preparation process thereof comprise the following steps: step 1, weighing 3 parts of Huupu white mud, 12 parts of Qinzhou Nixing pottery clay, 5 parts of water, 1-2 parts of aluminum oxide, 0.2-0.5 part of potassium oxide, 0.5-0.7 part of iron oxide, 1-1.2 parts of magnesium oxide and 0.5-0.8 part of calcium oxide; step 2, putting the Hupu white mud, the Qinzhou Nixing pottery clay, the aluminum oxide, the potassium oxide, the iron oxide, the magnesium oxide and the calcium oxide into a pottery clay stirring machine in sequence, then adding purified water into the pottery clay stirring machine, and starting the pottery clay stirring machine to stir the raw materials. The pottery clay is continuously beaten, so that the pottery clay is uniformly mixed, the ductility of the mixture is enhanced, and the plasticity of the mixture can be enhanced by adding chlorinated paraffin before beating, so that the mixed pottery clay has excellent plasticity and ductility.
本发明提供一种合浦白泥与钦州坭兴陶土组合配方及其制备工艺，涉及陶瓷坯料生产技术领域。该一种合浦白泥与钦州坭兴陶土组合配方及其制备工艺，包括以下步骤：步骤一、称取合浦白泥3份、钦州坭兴陶土12份、水5份、氧化铝1‑2份、氧化钾0.2‑0.5份、氧化铁0.5‑0.7份、氧化镁1‑1.2份、氧化钙0.5‑0.8份；步骤二、将合浦白泥、钦州坭兴陶土、氧化铝、氧化钾、氧化铁、氧化镁、氧化钙按照顺序放入陶土搅拌机内部，之后向陶土搅拌机内部加入纯净水后开启陶土搅拌机对原料进行搅拌。通过对其进行不断捶打，使其均匀混合的同时增强了混合物的延展性能，且在捶打前加入氯化石蜡能够增强混合物的可塑性能，使混合完成后的陶土具有优秀的可塑性与延展性。
Combination formula of Hupu white mud and Qinzhou Nixing pottery clay and preparation process thereof
The invention provides a combined formula of Hupu white mud and Qinzhou Nixing pottery clay and a preparation process of the combined formula, and relates to the technical field of ceramic blank production. The Huupu white mud and Qinzhou Nixing pottery clay combined formula and the preparation process thereof comprise the following steps: step 1, weighing 3 parts of Huupu white mud, 12 parts of Qinzhou Nixing pottery clay, 5 parts of water, 1-2 parts of aluminum oxide, 0.2-0.5 part of potassium oxide, 0.5-0.7 part of iron oxide, 1-1.2 parts of magnesium oxide and 0.5-0.8 part of calcium oxide; step 2, putting the Hupu white mud, the Qinzhou Nixing pottery clay, the aluminum oxide, the potassium oxide, the iron oxide, the magnesium oxide and the calcium oxide into a pottery clay stirring machine in sequence, then adding purified water into the pottery clay stirring machine, and starting the pottery clay stirring machine to stir the raw materials. The pottery clay is continuously beaten, so that the pottery clay is uniformly mixed, the ductility of the mixture is enhanced, and the plasticity of the mixture can be enhanced by adding chlorinated paraffin before beating, so that the mixed pottery clay has excellent plasticity and ductility.
本发明提供一种合浦白泥与钦州坭兴陶土组合配方及其制备工艺，涉及陶瓷坯料生产技术领域。该一种合浦白泥与钦州坭兴陶土组合配方及其制备工艺，包括以下步骤：步骤一、称取合浦白泥3份、钦州坭兴陶土12份、水5份、氧化铝1‑2份、氧化钾0.2‑0.5份、氧化铁0.5‑0.7份、氧化镁1‑1.2份、氧化钙0.5‑0.8份；步骤二、将合浦白泥、钦州坭兴陶土、氧化铝、氧化钾、氧化铁、氧化镁、氧化钙按照顺序放入陶土搅拌机内部，之后向陶土搅拌机内部加入纯净水后开启陶土搅拌机对原料进行搅拌。通过对其进行不断捶打，使其均匀混合的同时增强了混合物的延展性能，且在捶打前加入氯化石蜡能够增强混合物的可塑性能，使混合完成后的陶土具有优秀的可塑性与延展性。
Combination formula of Hupu white mud and Qinzhou Nixing pottery clay and preparation process thereof
一种合浦白泥与钦州坭兴陶土组合配方及其制备工艺
LIU YUANJING (Autor:in) / SU CHAOHUA (Autor:in) / LI ZHAOLIAN (Autor:in)
15.11.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Nixing pottery clay partial pressure type pressing process
| Europäisches Patentamt | 2020
Inlaying and clay-strip forming method Nixing pottery
| Europäisches Patentamt | 2016