Formula of medium-temperature blue-white colored pekoe glaze and method for manufacturing ceramic by using formula of medium-temperature blue-white colored pekoe glaze
The invention relates to a formula of medium-temperature blue-white colored pekoe glaze and a method for manufacturing ceramic by using the formula in the technical field of rabbit pekoe glaze. The formula comprises the following materials: 30-45 parts of feldspar; 10 to 13 parts of dolomite; 8 to 13 parts of calcite; 20-25 parts of quartz and 6-10 parts of talc; 5-8 parts of Guizhou soil; 3-5 parts of barium carbonate; 6-7 parts of cobalt black; 25 to 30 parts of potassium feldspar; 10 to 15 parts of calcite; 10 to 15 parts of zinc oxide; 10 to 14 parts of dolomite; 10 to 15 parts of spodumene; 10 to 15 parts of quartz; 3-5 parts of lithium carbonate; 3-5 parts of talc; 5-8 parts of titanium oxide; 20 to 25 parts of albite; 20 to 25 parts of calcite; 20 to 25 parts of spodumene; 3-5 parts of lithium carbonate; 4-6 parts of barium carbonate; 20 to 25 parts of quartz; the preparation method comprises the following steps: S1, preparing materials; s2, preparing a glaze material; s3, drying and observing; (S4); through the improvement and innovation of the existing operation technology and the increasingly stable sintering curve of the kiln and the sintering temperature in the kiln, the manufactured product not only has the characteristics of the rabbit hair, but also can present more colors and effects according to the difference of the added oxides.
本发明涉及兔毫釉技术领域的中温蓝白彩毫釉的配方及其使用该配方来制作陶瓷的方法，包括以下材料：长石30‑45份；白云石10‑13份；方解石8‑13份；石英20‑25份，滑石6‑10份；贵州土5‑8份；碳酸钡3‑5份；钴黑6‑7份；钾长石25‑30份；方解石10‑15份；氧化锌10‑15份；白云石10‑14份；锂辉石10‑15份；石英10‑15份；碳酸锂3‑5份；滑石3‑5份；氧化钛5‑8份；钠长石20‑25份；方解石20‑25份；锂辉石20‑25份；碳酸锂3‑5份；碳酸钡4‑6份；石英20‑25份；氧化钴1.5‑2.5份，包括以下步骤：S1，准备材料；S2，制备釉料；S3，烘干观察；S4；烧制成型，通过现在操作技术的改进创新，以及窑炉烧成曲线与窑内烧成温度的越来越稳定，制作出来的产品不仅有兔毫的特性，而且能够根据加入的氧化物的不同，能够呈现更多的颜色与效果。
Formula of medium-temperature blue-white colored pekoe glaze and method for manufacturing ceramic by using formula of medium-temperature blue-white colored pekoe glaze
The invention relates to a formula of medium-temperature blue-white colored pekoe glaze and a method for manufacturing ceramic by using the formula in the technical field of rabbit pekoe glaze. The formula comprises the following materials: 30-45 parts of feldspar; 10 to 13 parts of dolomite; 8 to 13 parts of calcite; 20-25 parts of quartz and 6-10 parts of talc; 5-8 parts of Guizhou soil; 3-5 parts of barium carbonate; 6-7 parts of cobalt black; 25 to 30 parts of potassium feldspar; 10 to 15 parts of calcite; 10 to 15 parts of zinc oxide; 10 to 14 parts of dolomite; 10 to 15 parts of spodumene; 10 to 15 parts of quartz; 3-5 parts of lithium carbonate; 3-5 parts of talc; 5-8 parts of titanium oxide; 20 to 25 parts of albite; 20 to 25 parts of calcite; 20 to 25 parts of spodumene; 3-5 parts of lithium carbonate; 4-6 parts of barium carbonate; 20 to 25 parts of quartz; the preparation method comprises the following steps: S1, preparing materials; s2, preparing a glaze material; s3, drying and observing; (S4); through the improvement and innovation of the existing operation technology and the increasingly stable sintering curve of the kiln and the sintering temperature in the kiln, the manufactured product not only has the characteristics of the rabbit hair, but also can present more colors and effects according to the difference of the added oxides.
本发明涉及兔毫釉技术领域的中温蓝白彩毫釉的配方及其使用该配方来制作陶瓷的方法，包括以下材料：长石30‑45份；白云石10‑13份；方解石8‑13份；石英20‑25份，滑石6‑10份；贵州土5‑8份；碳酸钡3‑5份；钴黑6‑7份；钾长石25‑30份；方解石10‑15份；氧化锌10‑15份；白云石10‑14份；锂辉石10‑15份；石英10‑15份；碳酸锂3‑5份；滑石3‑5份；氧化钛5‑8份；钠长石20‑25份；方解石20‑25份；锂辉石20‑25份；碳酸锂3‑5份；碳酸钡4‑6份；石英20‑25份；氧化钴1.5‑2.5份，包括以下步骤：S1，准备材料；S2，制备釉料；S3，烘干观察；S4；烧制成型，通过现在操作技术的改进创新，以及窑炉烧成曲线与窑内烧成温度的越来越稳定，制作出来的产品不仅有兔毫的特性，而且能够根据加入的氧化物的不同，能够呈现更多的颜色与效果。
Formula of medium-temperature blue-white colored pekoe glaze and method for manufacturing ceramic by using formula of medium-temperature blue-white colored pekoe glaze
中温蓝白彩毫釉的配方及其使用该配方来制作陶瓷的方法
WEN LI (Autor:in) / LAN QINGFU (Autor:in) / LIN GENG (Autor:in)
29.11.2022
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
Formula and preparation method of ceramic colored glaze
| Europäisches Patentamt | 2022