Formula of high-strength porcelain insulator active industrial alumina porcelain
The invention discloses a high-strength porcelain insulator active industrial alumina porcelain formula, which is prepared from the following components in parts by weight: 40 to 60 parts of flint clay, 40 to 100 parts of industrial alumina powder, 20 to 40 parts of silicon dioxide, 10 to 30 parts of quartz ore, 5 to 25 parts of mullite powder, 10 to 35 parts of clay, 5 to 10 parts of plasticizer, 0.5 to 2.5 parts of vermiculite powder and 0.1 to 1 part of potassium oxide. Comprising the following steps: S1, weighing raw materials, and sanding the raw materials to obtain blank particles with the diameter of 3-5 microns; by using the formula and the preparation steps for firing, the content of aluminum oxide in the sintered porcelain body is high, and the mechanical property and the chemical property of the porcelain body can be improved.
本发明公开了一种高强度瓷绝缘子活性工业氧化铝瓷配方，其包括以下重量份的组分组成：焦宝石40‑60份、工业氧化铝粉40～100份，二氧化硅20～40份，石英矿10～30份，莫来石粉5～25份，黏土10～35份，增塑剂5～10份，蛭石粉0.5～2.5份，氧化钾0.1～1份，所述高强度瓷绝缘子活性工业氧化铝瓷制备，包括以下步骤：S1：取原料进行称取，然后对其进行砂磨，得到直径为3‑5微米的坯料颗粒。通过使用本配方及制备步骤进行烧制，烧结后的瓷体中的氧化铝含量高，可以提高瓷体的力学性能和化学性能。
Formula of high-strength porcelain insulator active industrial alumina porcelain
The invention discloses a high-strength porcelain insulator active industrial alumina porcelain formula, which is prepared from the following components in parts by weight: 40 to 60 parts of flint clay, 40 to 100 parts of industrial alumina powder, 20 to 40 parts of silicon dioxide, 10 to 30 parts of quartz ore, 5 to 25 parts of mullite powder, 10 to 35 parts of clay, 5 to 10 parts of plasticizer, 0.5 to 2.5 parts of vermiculite powder and 0.1 to 1 part of potassium oxide. Comprising the following steps: S1, weighing raw materials, and sanding the raw materials to obtain blank particles with the diameter of 3-5 microns; by using the formula and the preparation steps for firing, the content of aluminum oxide in the sintered porcelain body is high, and the mechanical property and the chemical property of the porcelain body can be improved.
本发明公开了一种高强度瓷绝缘子活性工业氧化铝瓷配方，其包括以下重量份的组分组成：焦宝石40‑60份、工业氧化铝粉40～100份，二氧化硅20～40份，石英矿10～30份，莫来石粉5～25份，黏土10～35份，增塑剂5～10份，蛭石粉0.5～2.5份，氧化钾0.1～1份，所述高强度瓷绝缘子活性工业氧化铝瓷制备，包括以下步骤：S1：取原料进行称取，然后对其进行砂磨，得到直径为3‑5微米的坯料颗粒。通过使用本配方及制备步骤进行烧制，烧结后的瓷体中的氧化铝含量高，可以提高瓷体的力学性能和化学性能。
Formula of high-strength porcelain insulator active industrial alumina porcelain
一种高强度瓷绝缘子活性工业氧化铝瓷配方
ZHAO MINGBIAO (Autor:in) / SUN WEI (Autor:in) / XIAO BO (Autor:in) / XU NA (Autor:in) / HU HOUJIN (Autor:in)
31.01.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Formula of high-strength porcelain for manufacturing of suspension porcelain insulator
| Europäisches Patentamt | 2016
High-performance column type porcelain insulator formula and porcelain insulator thereof
| Europäisches Patentamt | 2023
Alumina-based porcelain insulator porcelain body and preparation method thereof
| Europäisches Patentamt | 2024