Sliding plate brick and preparation method thereof
The invention discloses a sliding plate brick and a preparation method thereof, and belongs to the field of new material preparation. The sliding plate brick comprises the following components in percentage by mass: a carbon fiber woven body, 60-80 wt% of mullite powder, 10-20 wt% of aluminum oxide powder, 2-3 wt% of carbon black and 10-30 wt% of zirconium oxide powder, wherein the sum of the mass fractions of the components is 100 wt%. The sliding plate brick containing the ceramic coating is prepared according to the steps of slurry preparation, vacuum grouting, drying, pressureless sintering and coating preparation. The ceramic coating is prepared on the surface of the sliding plate brick material, so that the use temperature and the service life of the sliding plate brick can be remarkably improved.
本发明公开了一种滑板砖及其制备方法，属于新材料制备领域。滑板砖组成成分及各组分质量分数为：碳纤维编织体，60～80wt％的莫来石粉体，10～20wt％的氧化铝粉体，2～3wt％的炭黑，10～30wt％的氧化锆粉体，各组分质量分数之和为100wt％。按照浆料的制备、真空注浆、干燥、无压烧结和涂层制备的步骤制备含陶瓷涂层的滑板砖。本发明在滑板砖材料表面制备陶瓷涂层，能显著提升滑板砖的使用温度和寿命。
Sliding plate brick and preparation method thereof
The invention discloses a sliding plate brick and a preparation method thereof, and belongs to the field of new material preparation. The sliding plate brick comprises the following components in percentage by mass: a carbon fiber woven body, 60-80 wt% of mullite powder, 10-20 wt% of aluminum oxide powder, 2-3 wt% of carbon black and 10-30 wt% of zirconium oxide powder, wherein the sum of the mass fractions of the components is 100 wt%. The sliding plate brick containing the ceramic coating is prepared according to the steps of slurry preparation, vacuum grouting, drying, pressureless sintering and coating preparation. The ceramic coating is prepared on the surface of the sliding plate brick material, so that the use temperature and the service life of the sliding plate brick can be remarkably improved.
本发明公开了一种滑板砖及其制备方法，属于新材料制备领域。滑板砖组成成分及各组分质量分数为：碳纤维编织体，60～80wt％的莫来石粉体，10～20wt％的氧化铝粉体，2～3wt％的炭黑，10～30wt％的氧化锆粉体，各组分质量分数之和为100wt％。按照浆料的制备、真空注浆、干燥、无压烧结和涂层制备的步骤制备含陶瓷涂层的滑板砖。本发明在滑板砖材料表面制备陶瓷涂层，能显著提升滑板砖的使用温度和寿命。
Sliding plate brick and preparation method thereof
一种滑板砖及其制备方法
YU XIPING (Autor:in) / ZHAO FENG (Autor:in) / GUI KAIXUAN (Autor:in) / RAN SONGLIN (Autor:in)
07.03.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Magnesium-spinel sliding plate brick and preparation method thereof
| Europäisches Patentamt | 2020
Low-carbon magnesia spinel sliding plate brick and preparation method thereof
| Europäisches Patentamt | 2022
Unfired pouring corundum spinel sliding plate brick and preparation method thereof
| Europäisches Patentamt | 2024