Pingyang oil drop glaze and preparation method thereof
The invention relates to the technical field of ceramic products, in particular to Pingyang oil drop glaze and a preparation method thereof. The raw materials comprise, by mass, 93%-94% of loess, 0.8%-1.2% of manganese oxide, 1.8%-3.2% of hematite powder and 2.8%-3.3% of talc. The loess is taken from Jinyu Riyun in Yao-Du district, Fen City, Shanxi, and mainly comprises the following components: 50-60% of SiO2, 9-12% of Al2O3, 7-10% of CaO, 1-3% of MgO, 4-5% of Fe2O3 and 2% of K2O; the main component of the hematite powder is Fe2O3; the talc is taken from the sea city of Liaoning Province, and the main components of the talc comprise 3MgO-4SiO2-H2O, Al2O3-FeO and Al2O3-MgO. The raw materials are simple, oil drop stripes are easily formed, the size is uniform, additives such as lead oxide are not used, and damage to the human body due to long-term use is avoided.
本发明涉及陶瓷制品技术领域，更具体而言，涉及一种平阳油滴釉及其制备方法。原材料质量百分比为93‑94％的黄土、0.8‑1.2％的氧化锰、1.8‑3.2％的赤铁矿粉和2.8‑3.3％的滑石。黄土取自山西临汾市尧都区金殿峪里村，其主要成分包括50‑60％的SiO2、9‑12％的Al2O3、7‑10％的CaO，1‑3％的MgO，4‑5％的Fe2O3和2％的K2O；所述赤铁矿粉主要成分为Fe2O3；所述滑石取自辽宁省海城市，其主要成分包括3MgO‑4SiO2‑H2O，Al2O3‑FeO和Al2O3‑MgO。本发明原料简单易形成“油滴斑纹”且大小均匀，不使用氧化铅等添加剂，不会因长期使用对人体造成损伤。
Pingyang oil drop glaze and preparation method thereof
The invention relates to the technical field of ceramic products, in particular to Pingyang oil drop glaze and a preparation method thereof. The raw materials comprise, by mass, 93%-94% of loess, 0.8%-1.2% of manganese oxide, 1.8%-3.2% of hematite powder and 2.8%-3.3% of talc. The loess is taken from Jinyu Riyun in Yao-Du district, Fen City, Shanxi, and mainly comprises the following components: 50-60% of SiO2, 9-12% of Al2O3, 7-10% of CaO, 1-3% of MgO, 4-5% of Fe2O3 and 2% of K2O; the main component of the hematite powder is Fe2O3; the talc is taken from the sea city of Liaoning Province, and the main components of the talc comprise 3MgO-4SiO2-H2O, Al2O3-FeO and Al2O3-MgO. The raw materials are simple, oil drop stripes are easily formed, the size is uniform, additives such as lead oxide are not used, and damage to the human body due to long-term use is avoided.
本发明涉及陶瓷制品技术领域，更具体而言，涉及一种平阳油滴釉及其制备方法。原材料质量百分比为93‑94％的黄土、0.8‑1.2％的氧化锰、1.8‑3.2％的赤铁矿粉和2.8‑3.3％的滑石。黄土取自山西临汾市尧都区金殿峪里村，其主要成分包括50‑60％的SiO2、9‑12％的Al2O3、7‑10％的CaO，1‑3％的MgO，4‑5％的Fe2O3和2％的K2O；所述赤铁矿粉主要成分为Fe2O3；所述滑石取自辽宁省海城市，其主要成分包括3MgO‑4SiO2‑H2O，Al2O3‑FeO和Al2O3‑MgO。本发明原料简单易形成“油滴斑纹”且大小均匀，不使用氧化铅等添加剂，不会因长期使用对人体造成损伤。
Pingyang oil drop glaze and preparation method thereof
一种平阳油滴釉及其制备方法
DUAN YUGUANG (Autor:in) / DONG TING (Autor:in)
04.04.2023
Patent
Elektronische Ressource
Chinesisch
Oil-drop temmoku glaze and firing method of oil-drop temmoku glaze ceramic
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2021
Cracked glaze, preparation method thereof and sanitary ceramic containing cracked glaze
| Europäisches Patentamt | 2024
Transmutation glaze, transmutation glaze laterite ceramic product and preparation method thereof
| Europäisches Patentamt | 2022