Ru porcelain for white spirit curing and preparation method thereof
The invention relates to white spirit curing, in particular to Ru porcelain for white spirit curing and a preparation method thereof.The Ru porcelain comprises a Ru porcelain biscuit and a coating, and the coating is smeared on the inner wall of the Ru porcelain biscuit; the coating comprises 20-30 parts of calcium carbonate powder, 4-8 parts of epoxy resin, 1-3 parts of a curing agent, 2-3 parts of a curing agent, 10-15 parts of water and 3-5 parts of a pore forming agent; the preparation method of the curing agent comprises the following steps: 1) mixing attapulgite with a hydrochloric acid solution, filtering, cleaning and drying to obtain a pretreated material; and 2) mixing ferric nitrate with water to prepare a mixed solution, mixing the pretreated material prepared in the step 1) with the mixed solution, oscillating at a constant temperature of 20-30 DEG C for 30-50 minutes, taking out, roasting at a high temperature, and grinding to obtain the Ru porcelain container.
本发明涉及白酒熟化的，特别涉及一种用于白酒熟化的汝瓷及其制备方法，包括汝瓷素胚和涂层，所述涂层涂抹在汝瓷素胚的内壁上；所述涂层包括碳酸钙粉20‑30份，环氧树脂4‑8份，熟化剂1‑3份，固化剂2‑3份，水10‑15份，造孔剂3‑5份；所述熟化剂的制备方法包括如下步骤：1）取凹凸棒土与盐酸溶液混合、过滤、清洗、干燥制得预处理料；2）取硝酸铁与水混合制备成混合液，将步骤1）中制得的预处理料与混合液混合，20‑30℃下恒温震荡30‑50min，取出高温焙烧，研磨即得。本申请具有提高汝瓷容器对白酒熟化效果的优点。
Ru porcelain for white spirit curing and preparation method thereof
The invention relates to white spirit curing, in particular to Ru porcelain for white spirit curing and a preparation method thereof.The Ru porcelain comprises a Ru porcelain biscuit and a coating, and the coating is smeared on the inner wall of the Ru porcelain biscuit; the coating comprises 20-30 parts of calcium carbonate powder, 4-8 parts of epoxy resin, 1-3 parts of a curing agent, 2-3 parts of a curing agent, 10-15 parts of water and 3-5 parts of a pore forming agent; the preparation method of the curing agent comprises the following steps: 1) mixing attapulgite with a hydrochloric acid solution, filtering, cleaning and drying to obtain a pretreated material; and 2) mixing ferric nitrate with water to prepare a mixed solution, mixing the pretreated material prepared in the step 1) with the mixed solution, oscillating at a constant temperature of 20-30 DEG C for 30-50 minutes, taking out, roasting at a high temperature, and grinding to obtain the Ru porcelain container.
本发明涉及白酒熟化的，特别涉及一种用于白酒熟化的汝瓷及其制备方法，包括汝瓷素胚和涂层，所述涂层涂抹在汝瓷素胚的内壁上；所述涂层包括碳酸钙粉20‑30份，环氧树脂4‑8份，熟化剂1‑3份，固化剂2‑3份，水10‑15份，造孔剂3‑5份；所述熟化剂的制备方法包括如下步骤：1）取凹凸棒土与盐酸溶液混合、过滤、清洗、干燥制得预处理料；2）取硝酸铁与水混合制备成混合液，将步骤1）中制得的预处理料与混合液混合，20‑30℃下恒温震荡30‑50min，取出高温焙烧，研磨即得。本申请具有提高汝瓷容器对白酒熟化效果的优点。
Ru porcelain for white spirit curing and preparation method thereof
一种用于白酒熟化的汝瓷及其制备方法
TANG PEIYUAN (Autor:in) / ZHANG HAIJUN (Autor:in)
07.04.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Crystal white porcelain blank and preparation method thereof
| Europäisches Patentamt | 2023
High-toughness white porcelain and preparation method thereof
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2020
Negative ion antibacterial white porcelain and preparation method thereof
| Europäisches Patentamt | 2021
Ultra-white porcelain polished marble and preparation method thereof
| Europäisches Patentamt | 2020