Firing method for smoldering black pottery in electric kiln
The invention discloses a firing method for smoldering black pottery in an electric kiln, which is characterized in that high-temperature ceramic pug with the plasticity index of 10-15 is used as a blank making raw material, wood (such as pine) with higher oiliness is used as a carburizing material, and firing is carried out in a conventional high-temperature electric kiln. The firing step comprises the steps of green body forming, green body drying, green body finishing, green body boxing, timber boxing and electric kiln firing. By means of the arrangement, manufacturing of smoldering black pottery in the electric kiln can be achieved, after smoldering carburization is conducted on the manufactured black pottery, the color of the manufactured black pottery is mainly matte black, has falling ash glaze spots and is natural and rich, chromatic aberration changes are generated by controlling pine wood materials in the sagger, the manufactured black pottery is hard in body quality and clear in sound, and a good artistic effect can be achieved.
本发明公开了一种电窑焖烧黑陶的烧制方法，其中，以塑性指数在10‑15之间的高温陶瓷泥料为制坯原料，以油性较大的木料（如松木）为渗碳材料，以常规高温电窑进行烧制。烧制步骤包括：坯体成型、坯体干燥、坯体修整、坯体装匣、木料装匣、电窑烧制。如此设置，可以实现电窑焖烧黑陶的制作，所制作的黑陶经过焖烧渗碳后，其色泽以哑光黑色为主，带有落灰釉斑，色泽自然丰富，通过控制匣钵内松柴材料产生色差变化，所制黑陶胎质坚硬，声音清脆，可以得到很好的艺术效果。
Firing method for smoldering black pottery in electric kiln
The invention discloses a firing method for smoldering black pottery in an electric kiln, which is characterized in that high-temperature ceramic pug with the plasticity index of 10-15 is used as a blank making raw material, wood (such as pine) with higher oiliness is used as a carburizing material, and firing is carried out in a conventional high-temperature electric kiln. The firing step comprises the steps of green body forming, green body drying, green body finishing, green body boxing, timber boxing and electric kiln firing. By means of the arrangement, manufacturing of smoldering black pottery in the electric kiln can be achieved, after smoldering carburization is conducted on the manufactured black pottery, the color of the manufactured black pottery is mainly matte black, has falling ash glaze spots and is natural and rich, chromatic aberration changes are generated by controlling pine wood materials in the sagger, the manufactured black pottery is hard in body quality and clear in sound, and a good artistic effect can be achieved.
本发明公开了一种电窑焖烧黑陶的烧制方法，其中，以塑性指数在10‑15之间的高温陶瓷泥料为制坯原料，以油性较大的木料（如松木）为渗碳材料，以常规高温电窑进行烧制。烧制步骤包括：坯体成型、坯体干燥、坯体修整、坯体装匣、木料装匣、电窑烧制。如此设置，可以实现电窑焖烧黑陶的制作，所制作的黑陶经过焖烧渗碳后，其色泽以哑光黑色为主，带有落灰釉斑，色泽自然丰富，通过控制匣钵内松柴材料产生色差变化，所制黑陶胎质坚硬，声音清脆，可以得到很好的艺术效果。
Firing method for smoldering black pottery in electric kiln
一种电窑焖烧黑陶的烧制方法
LI HUIDONG (Autor:in) / ZHANG ZHELI (Autor:in)
25.04.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Kiln for firing of decorations on pottery ware
Engineering Index Backfile | 1955
Pottery firing process based on reverse flame type firewood firing dragon kiln
| Europäisches Patentamt | 2024
A new type of tunnel kiln for firing pottery
| Engineering Index Backfile | 1928