The invention provides a preparation method of mildew-proof long-acting antibacterial quartz stone. The preparation method comprises the following steps: 1) uniformly stirring and mixing 30-80 parts by weight of quartz sand added with an antibacterial modifier, 5-25 parts by weight of shells, 5-25 parts by weight of cullet, 10-30 parts by weight of unsaturated resin, 6-15 parts by weight of a curing agent, 3-10 parts by weight of a dispersing agent, 2-7 parts by weight of a coupling agent and 2-7 parts by weight of a surfactant; the preparation method comprises the following steps of (1) mixing the raw materials, (2) uniformly spreading the mixed raw materials on a template, (3) carrying out compression molding on the template under the pressure of-0.15 to-0.05 MPa, (4) curing the molded plate for 1-3 hours at the temperature of 85-115 DEG C, and (5) carrying out demolding, stacking and cooling on the cured plate to obtain the antibacterial quartzite. The antibacterial quartzite prepared by the preparation method disclosed by the invention is good in wear resistance and antibacterial performance.
本发明提供防霉长效抗菌型石英石制备方法，包括步骤1）将30～80重量份的添加抗菌改性剂的石英砂、5～25重量份的贝壳、5～25重量份的碎玻璃、10～30重量份的不饱和树脂、6～15重量份的固化剂、3～10重量份的分散剂、2～7重量份的偶联剂、2～7重量份的表面活性剂搅拌混合均匀；2）将上述混合好的原料均匀平铺在模板上；3）将模板在‑0.15～‑0.05MPa下压制成型；4）将成型后的板材在85～115℃下固化1～3小时；5)将上述固化后的板材进行脱模，堆放冷却后，即可得到所述抗菌石英石，通过本发明制备的抗菌石英石耐磨性、抗菌性能好。
The invention provides a preparation method of mildew-proof long-acting antibacterial quartz stone. The preparation method comprises the following steps: 1) uniformly stirring and mixing 30-80 parts by weight of quartz sand added with an antibacterial modifier, 5-25 parts by weight of shells, 5-25 parts by weight of cullet, 10-30 parts by weight of unsaturated resin, 6-15 parts by weight of a curing agent, 3-10 parts by weight of a dispersing agent, 2-7 parts by weight of a coupling agent and 2-7 parts by weight of a surfactant; the preparation method comprises the following steps of (1) mixing the raw materials, (2) uniformly spreading the mixed raw materials on a template, (3) carrying out compression molding on the template under the pressure of-0.15 to-0.05 MPa, (4) curing the molded plate for 1-3 hours at the temperature of 85-115 DEG C, and (5) carrying out demolding, stacking and cooling on the cured plate to obtain the antibacterial quartzite. The antibacterial quartzite prepared by the preparation method disclosed by the invention is good in wear resistance and antibacterial performance.
本发明提供防霉长效抗菌型石英石制备方法，包括步骤1）将30～80重量份的添加抗菌改性剂的石英砂、5～25重量份的贝壳、5～25重量份的碎玻璃、10～30重量份的不饱和树脂、6～15重量份的固化剂、3～10重量份的分散剂、2～7重量份的偶联剂、2～7重量份的表面活性剂搅拌混合均匀；2）将上述混合好的原料均匀平铺在模板上；3）将模板在‑0.15～‑0.05MPa下压制成型；4）将成型后的板材在85～115℃下固化1～3小时；5)将上述固化后的板材进行脱模，堆放冷却后，即可得到所述抗菌石英石，通过本发明制备的抗菌石英石耐磨性、抗菌性能好。
Preparation method of mildew-proof long-acting antibacterial quartz stone
防霉长效抗菌型石英石制备方法
02.06.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Mildew-proof antibacterial inorganic artificial stone and preparation method thereof
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2022
Pressure-proof antibacterial artificial quartz stone plate and preparation method thereof
| Europäisches Patentamt | 2015
Long-acting antibacterial artificial stone and preparation method thereof
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2024