Construction method of cruise ship kitchen ceramic tiles meeting USPH standard requirements
The embodiment of the invention discloses a cruise ship kitchen ceramic tile construction method capable of meeting USPH standard requirements, which comprises the following steps: carrying out joint filling treatment on a sealing welding plate in a temperature range of more than 15 DEG C and less than 35 DEG C; the upper layer of the sealed welding plate is coated with a primer adhesion agent, and drying is conducted for 1-4 hours; laying mortar on the seal welding plate coated with the primer adhesion agent in a temperature range of more than 5 DEG C and less than 35 DEG C; laying a flat layer on the sealed welding plate on which the mortar is laid, and drying for 24-72 hours; coating primer on the seal welding plate paved with the flat layer, and drying for 1-4 hours; ceramic tile cement is laid on the seal welding plate coated with the primer, and drying is conducted for 10-14 hours; ceramic tiles are pasted on the dried ceramic tile cement; gaps formed by the attached ceramic tiles are grouted, and drying is conducted for 10-14 hours; and performing peripheral resin grouting on the gap after grouting operation, and drying for 24 hours.
本发明实施例公开了一种满足USPH规范要求的邮轮厨房瓷砖施工方法，包括在大于15℃小于35℃的温度范围内，对密封焊接板材进行填缝处理；在密封焊接板材的上层涂抹底漆界面剂，并干燥1‑4小时；在大于5℃小于35℃的温度范围内，在涂抹了底漆界面剂的密封焊接板材上铺设砂浆；在铺设了砂浆的密封焊接板材上铺设平层，并干燥24‑72小时；在铺设了平层的密封焊接板材上涂抹底漆，并干燥1‑4小时；在涂抹了底漆的密封焊接板材上铺设瓷砖水泥，并干燥10‑14小时；在干燥后的瓷砖水泥上贴设瓷砖；对贴合的瓷砖所形成的缝隙进行灌浆，并干燥10‑14小时；在已进行灌浆作业后的缝隙处进行周边树脂灌浆，并干燥24小时。
Construction method of cruise ship kitchen ceramic tiles meeting USPH standard requirements
The embodiment of the invention discloses a cruise ship kitchen ceramic tile construction method capable of meeting USPH standard requirements, which comprises the following steps: carrying out joint filling treatment on a sealing welding plate in a temperature range of more than 15 DEG C and less than 35 DEG C; the upper layer of the sealed welding plate is coated with a primer adhesion agent, and drying is conducted for 1-4 hours; laying mortar on the seal welding plate coated with the primer adhesion agent in a temperature range of more than 5 DEG C and less than 35 DEG C; laying a flat layer on the sealed welding plate on which the mortar is laid, and drying for 24-72 hours; coating primer on the seal welding plate paved with the flat layer, and drying for 1-4 hours; ceramic tile cement is laid on the seal welding plate coated with the primer, and drying is conducted for 10-14 hours; ceramic tiles are pasted on the dried ceramic tile cement; gaps formed by the attached ceramic tiles are grouted, and drying is conducted for 10-14 hours; and performing peripheral resin grouting on the gap after grouting operation, and drying for 24 hours.
本发明实施例公开了一种满足USPH规范要求的邮轮厨房瓷砖施工方法，包括在大于15℃小于35℃的温度范围内，对密封焊接板材进行填缝处理；在密封焊接板材的上层涂抹底漆界面剂，并干燥1‑4小时；在大于5℃小于35℃的温度范围内，在涂抹了底漆界面剂的密封焊接板材上铺设砂浆；在铺设了砂浆的密封焊接板材上铺设平层，并干燥24‑72小时；在铺设了平层的密封焊接板材上涂抹底漆，并干燥1‑4小时；在涂抹了底漆的密封焊接板材上铺设瓷砖水泥，并干燥10‑14小时；在干燥后的瓷砖水泥上贴设瓷砖；对贴合的瓷砖所形成的缝隙进行灌浆，并干燥10‑14小时；在已进行灌浆作业后的缝隙处进行周边树脂灌浆，并干燥24小时。
Construction method of cruise ship kitchen ceramic tiles meeting USPH standard requirements
一种满足USPH规范要求的邮轮厨房瓷砖施工方法
GUO NING (Autor:in) / FU JIANGQING (Autor:in) / ZHENG JUNPING (Autor:in)
14.07.2023
Patent
Elektronische Ressource
Chinesisch
Construction method for movably splicing ceramic tiles
| Europäisches Patentamt | 2023
Construction method for microcrystalline stone ceramic tiles
| Europäisches Patentamt | 2015
A METHOD FOR PRODUCING CERAMIC TILES, AND CERAMIC TILES
| Europäisches Patentamt | 2024
A METHOD FOR PRODUCING CERAMIC TILES, AND CERAMIC TILES
| Europäisches Patentamt | 2024