Low-temperature glaze and glazing process thereof
The invention provides low-temperature glaze and a glazing process thereof, and relates to the technical field of ceramic glaze. The low-temperature glaze comprises the following components in parts by weight: 90-100 parts of lead-boron-free low-temperature frit, 5-10 parts of Suzhou clay, 3-5 parts of a dispersing agent, 3-5 parts of lithium carbonate, 3-5 parts of boric acid, 32-38 parts of water and 6-10 parts of an organic binder. The low-temperature glaze disclosed by the invention is stable in quality, and can be vitrified at 650-700 DEG C to generate luster. The low-temperature glaze and the glazing process are mainly used in functional ceramic selenium-rich glaze ceramic and sterilized glaze ceramic, the adhesive force is strong, the innovation of vitrified tread glazing with zero water absorption is broken, and the ceramic strength can be improved.
本发明提供一种低温釉及其施釉工艺,涉及陶瓷釉料技术领域。一种低温釉,按重量份数计,包括:无铅硼低温熔块90‑100份,苏州土5‑10份,分散剂3‑5份,碳酸锂3‑5份,硼酸3‑5份,水32‑38份和有机粘结剂6‑10份。本发明的低温釉,质量稳定,能在650‑700℃玻化,产生光泽。低温釉以及施釉工艺主要用于功能陶瓷富硒釉陶瓷,灭菌釉陶瓷中,附着力强,打破了在瓷化、吸水率为零胎面施釉的创新,可以提高陶瓷强度。
Low-temperature glaze and glazing process thereof
The invention provides low-temperature glaze and a glazing process thereof, and relates to the technical field of ceramic glaze. The low-temperature glaze comprises the following components in parts by weight: 90-100 parts of lead-boron-free low-temperature frit, 5-10 parts of Suzhou clay, 3-5 parts of a dispersing agent, 3-5 parts of lithium carbonate, 3-5 parts of boric acid, 32-38 parts of water and 6-10 parts of an organic binder. The low-temperature glaze disclosed by the invention is stable in quality, and can be vitrified at 650-700 DEG C to generate luster. The low-temperature glaze and the glazing process are mainly used in functional ceramic selenium-rich glaze ceramic and sterilized glaze ceramic, the adhesive force is strong, the innovation of vitrified tread glazing with zero water absorption is broken, and the ceramic strength can be improved.
本发明提供一种低温釉及其施釉工艺,涉及陶瓷釉料技术领域。一种低温釉,按重量份数计,包括:无铅硼低温熔块90‑100份,苏州土5‑10份,分散剂3‑5份,碳酸锂3‑5份,硼酸3‑5份,水32‑38份和有机粘结剂6‑10份。本发明的低温釉,质量稳定,能在650‑700℃玻化,产生光泽。低温釉以及施釉工艺主要用于功能陶瓷富硒釉陶瓷,灭菌釉陶瓷中,附着力强,打破了在瓷化、吸水率为零胎面施釉的创新,可以提高陶瓷强度。
Low-temperature glaze and glazing process thereof
一种低温釉及其施釉工艺
SUN WEN (Autor:in) / ZHAO DANDAN (Autor:in) / CHEN YU (Autor:in) / SHI ZHANJIE (Autor:in)
18.07.2023
Patent
Elektronische Ressource
Chinesisch
Electroceramic composite glaze and glazing process thereof
Europäisches Patentamt | 2023
|Ceramic glaze with non-cracking glaze surface and glazing method thereof
Europäisches Patentamt | 2020
|