Electrolytic manganese residue ecological cement and preparation method thereof
The invention belongs to the technical field of building materials, and provides electrolytic manganese residue ecological cement and a preparation method thereof. The electrolytic manganese residue ecological cement comprises the following components in parts by weight: 50-60 parts of cement clinker, 10-20 parts of steel slag, 10-15 parts of electrolytic manganese residues, 1-5 parts of gypsum and 1-5 parts of an auxiliary agent. The preparation method of the electrolytic manganese residue ecological cement comprises the following steps: calcining electrolytic manganese residues to obtain pretreated electrolytic manganese residues; mixing cement clinker, steel slag, pretreated electrolytic manganese slag, gypsum and an auxiliary agent, and grinding to obtain mixed powder; and calcining the mixed powder to obtain the electrolytic manganese residue ecological cement. The preparation method is simple, the product quality is high, a large amount of accumulated electrolytic manganese residues are recycled, serious damage of the electrolytic manganese residues to the environment is relieved, and good economic, environmental and social benefits are achieved.
本发明属于建筑材料技术领域，本发明提供了一种电解锰渣生态水泥及其制备方法。该电解锰渣生态水泥包括以下重量份的组分：水泥熟料50～60份，钢渣10～20份，电解锰渣10～15份，石膏1～5份，助剂1～5份。该电解锰渣生态水泥的制备方法，包括以下步骤：将电解锰渣进行煅烧处理得到预处理电解锰渣；将水泥熟料、钢渣、预处理电解锰渣、石膏和助剂混合后进行研磨得到混合粉料；将混合粉料进行煅烧处理即得电解锰渣生态水泥。本发明的制备方法简单，产品质量高，使大量堆积的电解锰渣得到了大宗循环利用，减轻了电解锰渣对环境的严重破坏，并具有良好的经济、环境和社会效益。
Electrolytic manganese residue ecological cement and preparation method thereof
The invention belongs to the technical field of building materials, and provides electrolytic manganese residue ecological cement and a preparation method thereof. The electrolytic manganese residue ecological cement comprises the following components in parts by weight: 50-60 parts of cement clinker, 10-20 parts of steel slag, 10-15 parts of electrolytic manganese residues, 1-5 parts of gypsum and 1-5 parts of an auxiliary agent. The preparation method of the electrolytic manganese residue ecological cement comprises the following steps: calcining electrolytic manganese residues to obtain pretreated electrolytic manganese residues; mixing cement clinker, steel slag, pretreated electrolytic manganese slag, gypsum and an auxiliary agent, and grinding to obtain mixed powder; and calcining the mixed powder to obtain the electrolytic manganese residue ecological cement. The preparation method is simple, the product quality is high, a large amount of accumulated electrolytic manganese residues are recycled, serious damage of the electrolytic manganese residues to the environment is relieved, and good economic, environmental and social benefits are achieved.
本发明属于建筑材料技术领域，本发明提供了一种电解锰渣生态水泥及其制备方法。该电解锰渣生态水泥包括以下重量份的组分：水泥熟料50～60份，钢渣10～20份，电解锰渣10～15份，石膏1～5份，助剂1～5份。该电解锰渣生态水泥的制备方法，包括以下步骤：将电解锰渣进行煅烧处理得到预处理电解锰渣；将水泥熟料、钢渣、预处理电解锰渣、石膏和助剂混合后进行研磨得到混合粉料；将混合粉料进行煅烧处理即得电解锰渣生态水泥。本发明的制备方法简单，产品质量高，使大量堆积的电解锰渣得到了大宗循环利用，减轻了电解锰渣对环境的严重破坏，并具有良好的经济、环境和社会效益。
Electrolytic manganese residue ecological cement and preparation method thereof
一种电解锰渣生态水泥及其制备方法
WANG HAIFENG (Autor:in) / WANG JIAWEI (Autor:in)
21.07.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Electrolytic manganese residue super sulfate cement and preparation method thereof
| Europäisches Patentamt | 2024
Electrolytic manganese residue autoclaved brick and preparation method thereof
| Europäisches Patentamt | 2020
Electrolytic manganese residue sintered brick and preparation method thereof
| Europäisches Patentamt | 2022
Reinforced electrolytic manganese residue sintered brick and preparation method thereof
| Europäisches Patentamt | 2022