本发明公开了一种防破损耐火砖加工方法，该方法包括以下步骤：S1、原料的制备：固体原料制备；40‑55重量份铝矾土、10‑15重量份镁砂细颗粒、5‑10重量份半硅质粘土、2‑4重量份的硅藻土、5‑7重量份的刚玉粉和3‑5重量份的陶瓷颗粒；液态原料制备；10‑20重量份的清水、2‑4重量份的白乳胶、3‑5重量份酚醛树脂、1‑2重量份的硅溶胶和2‑4重量份的硅酸钠，本方法通过采用一定比例的铝矾土和镁砂细颗粒混合，添加陶瓷、刚玉粉和硅藻土等成份，能够有效的提升耐火砖的耐火能力，同时本耐火砖在制作砖坯时，采用的乳液进行混合，相比传统的砖坯，粘性更好，使得在砖坯在制作时不易破裂，砖坯成品率高。

The invention discloses a processing method of a breakage-proof refractory brick. The method comprises the following steps: S1, preparing raw materials: preparing solid raw materials; the refractory brick is prepared from, by weight, 40-55 parts of bauxite, 10-15 parts of magnesia fine particles, 5-10 parts of semi-siliceous clay, 2-4 parts of kieselguhr, 5-7 parts of corundum powder and 3-5 parts of ceramic particles. Preparing a liquid raw material; according to the method, the bauxite and the magnesia fine particles in a certain proportion are mixed, and the ceramic, the corundum powder, the diatomite and other components are added, so that the fire resistance of the refractory brick can be effectively improved; meanwhile, when the refractory brick is used for manufacturing a green brick, the emulsion is adopted for mixing, and compared with a traditional green brick, the viscidity is better, so that the green brick is not prone to breakage in the manufacturing process, and the green brick yield is high.