Chloride ion erosion and abrasion resistant mortar and preparation method and application thereof
The invention discloses chloride ion erosion and abrasion resistant mortar and a preparation method and application thereof, the chloride ion erosion and abrasion resistant mortar is a mixture of cement, water and fine aggregate, and the fine aggregate comprises sand and microcrystalline glass; the microcrystalline glass is prepared from the following components in parts by mass: 60 to 80 parts of SiO2, 1 to 30 parts of Al2O3, 0.5 to 2 parts of MgO, 1 to 3 parts of TiO2, 1 to 3 parts of ZnO, 1 to 3 parts of ZrO2, 1 to 3 parts of BaO and 1 to 4 parts of Li2O. The microcrystalline glass is high in chloride ion resistance and good in abrasion resistance.
本发明公开一种抗氯离子侵蚀和抗冲磨砂浆及其制备方法与应用,其为水泥、水、细骨料的混合物,所述细骨料包括砂和微晶玻璃;所述微晶玻璃包括质量份数如下的组分:60‑80份SiO2、1‑30份Al2O3、0.5‑2份MgO、1‑3份TiO2、1‑3份ZnO、1‑3份ZrO2、1‑3份BaO、1‑4份Li2O,抗氯离子性能强,抗冲磨效果好。
Chloride ion erosion and abrasion resistant mortar and preparation method and application thereof
The invention discloses chloride ion erosion and abrasion resistant mortar and a preparation method and application thereof, the chloride ion erosion and abrasion resistant mortar is a mixture of cement, water and fine aggregate, and the fine aggregate comprises sand and microcrystalline glass; the microcrystalline glass is prepared from the following components in parts by mass: 60 to 80 parts of SiO2, 1 to 30 parts of Al2O3, 0.5 to 2 parts of MgO, 1 to 3 parts of TiO2, 1 to 3 parts of ZnO, 1 to 3 parts of ZrO2, 1 to 3 parts of BaO and 1 to 4 parts of Li2O. The microcrystalline glass is high in chloride ion resistance and good in abrasion resistance.
本发明公开一种抗氯离子侵蚀和抗冲磨砂浆及其制备方法与应用,其为水泥、水、细骨料的混合物,所述细骨料包括砂和微晶玻璃;所述微晶玻璃包括质量份数如下的组分:60‑80份SiO2、1‑30份Al2O3、0.5‑2份MgO、1‑3份TiO2、1‑3份ZnO、1‑3份ZrO2、1‑3份BaO、1‑4份Li2O,抗氯离子性能强,抗冲磨效果好。
Chloride ion erosion and abrasion resistant mortar and preparation method and application thereof
一种抗氯离子侵蚀和抗冲磨砂浆及其制备方法与应用
RAO MEIJUAN (Autor:in) / GAO YU (Autor:in) / TANG XIAOWEI (Autor:in) / WANG FAZHOU (Autor:in) / YANG LU (Autor:in) / HU SHUGUANG (Autor:in)
27.10.2023
Patent
Elektronische Ressource
Chinesisch
Chloride ion erosion resistant composite cement mortar and preparation method thereof
Europäisches Patentamt | 2024
|Elastic epoxy mortar abrasion-resistant material and preparation method thereof
Europäisches Patentamt | 2021
|Europäisches Patentamt | 2022
|Erosion-resistant and corrosion-resistant ceramic resin mortar and preparation method thereof
Europäisches Patentamt | 2020
|Europäisches Patentamt | 2022
|