Low-shrinkage large-long undercounter ceramic green body and preparation method thereof
The invention relates to the technical field of sanitary ceramics, in particular to a low-shrinkage large-long undercounter ceramic green body and a preparation method thereof. Comprising the following raw materials in parts by mass: 1-3 parts of calcined talc, 5-8 parts of aluminum oxide, 30-40 parts of Fengyuan, 5-10 parts of high-strength soil, 12-16 parts of an additive base, 25-35 parts of black mud, 3-5 parts of flying soil, 8-12 parts of white mud and 0.5-1.5 parts of dolomite, the mass ratio of the aluminum oxide to the high-strength soil is 1: (1-1.5), and the high-strength soil is prepared by pulping, grouting, vacuumizing and pressure forming. The ceramic green body is good in quality, small in ceramic shrinkage rate, not prone to deformation and high in strength.
本申请涉及卫生陶瓷技术领域，尤其涉及一种低收缩率大长台下盆陶瓷坯体及其制备方法。包括以下质量份数的原料：烧滑石1‑3份，氧化铝5‑8份，丰源30‑40份，高强土5‑10份，加基12‑16份，黑泥25‑35份，飞天土3‑5份，白泥8‑12份，白云石0.5‑1.5份，其中，所述氧化铝和所述高强土的质量比为1:1‑1.5，通过制浆，注浆，抽真空，加压成型，烧成等工序获得一种质量好、陶瓷收缩率小、不易变形、强度高的低收缩率大长台下盆陶瓷坯体。
Low-shrinkage large-long undercounter ceramic green body and preparation method thereof
The invention relates to the technical field of sanitary ceramics, in particular to a low-shrinkage large-long undercounter ceramic green body and a preparation method thereof. Comprising the following raw materials in parts by mass: 1-3 parts of calcined talc, 5-8 parts of aluminum oxide, 30-40 parts of Fengyuan, 5-10 parts of high-strength soil, 12-16 parts of an additive base, 25-35 parts of black mud, 3-5 parts of flying soil, 8-12 parts of white mud and 0.5-1.5 parts of dolomite, the mass ratio of the aluminum oxide to the high-strength soil is 1: (1-1.5), and the high-strength soil is prepared by pulping, grouting, vacuumizing and pressure forming. The ceramic green body is good in quality, small in ceramic shrinkage rate, not prone to deformation and high in strength.
本申请涉及卫生陶瓷技术领域，尤其涉及一种低收缩率大长台下盆陶瓷坯体及其制备方法。包括以下质量份数的原料：烧滑石1‑3份，氧化铝5‑8份，丰源30‑40份，高强土5‑10份，加基12‑16份，黑泥25‑35份，飞天土3‑5份，白泥8‑12份，白云石0.5‑1.5份，其中，所述氧化铝和所述高强土的质量比为1:1‑1.5，通过制浆，注浆，抽真空，加压成型，烧成等工序获得一种质量好、陶瓷收缩率小、不易变形、强度高的低收缩率大长台下盆陶瓷坯体。
Low-shrinkage large-long undercounter ceramic green body and preparation method thereof
一种低收缩率大长台下盆陶瓷坯体及其制备方法
FENG HONGQIANG (Autor:in) / LI XIAOMAN (Autor:in)
10.11.2023
Patent
Elektronische Ressource
Chinesisch