Easy-to-clean glaze, sanitary ware and preparation method of easy-to-clean glaze
The invention discloses easy-to-clean glaze, sanitary ware and a preparation method thereof, and relates to the technical field of sanitary ware. The easy-to-clean glaze is prepared from the following raw materials in parts by mass: 15 to 22 parts of quartz powder, 8 to 15 parts of wollastonite, 25 to 40 parts of potassium feldspar, 3 to 10 parts of lithium carbonate and 15 to 30 parts of boron frit. The melting temperature of the boron frit is 1050-1160 DEG C, and the content of diboron trioxide in the boron frit is greater than or equal to 10% by mass. According to the easy-to-clean glaze, the roughness of a glaze surface can be remarkably reduced, the glaze surface is smooth and high in flatness, the glaze surface is not prone to absorbing dirt, the excellent easy-to-clean effect is achieved, and the problem that existing easy-to-clean glaze is still prone to absorbing dirt in the using process is solved.
本发明公开了一种易清洁釉料、卫生洁具及其制备方法，涉及卫生洁具技术领域。本发明的易清洁釉料包括以下质量份数的原料：石英粉15～22份、硅灰石8～15份、钾长石25～40份、碳酸锂3～10份和硼熔块15～30份；硼熔块的熔融温度为1050～1160℃，且按质量百分数计算，硼熔块中三氧化二硼的含量大于等于10％。本发明的易清洁釉料能显著降低釉面的粗糙度，使釉面光滑且平整度高，使釉面不易吸污，具备优异的易清洁效果，解决了现有易清洁釉在使用过程中仍存在容易吸污的问题。
Easy-to-clean glaze, sanitary ware and preparation method of easy-to-clean glaze
The invention discloses easy-to-clean glaze, sanitary ware and a preparation method thereof, and relates to the technical field of sanitary ware. The easy-to-clean glaze is prepared from the following raw materials in parts by mass: 15 to 22 parts of quartz powder, 8 to 15 parts of wollastonite, 25 to 40 parts of potassium feldspar, 3 to 10 parts of lithium carbonate and 15 to 30 parts of boron frit. The melting temperature of the boron frit is 1050-1160 DEG C, and the content of diboron trioxide in the boron frit is greater than or equal to 10% by mass. According to the easy-to-clean glaze, the roughness of a glaze surface can be remarkably reduced, the glaze surface is smooth and high in flatness, the glaze surface is not prone to absorbing dirt, the excellent easy-to-clean effect is achieved, and the problem that existing easy-to-clean glaze is still prone to absorbing dirt in the using process is solved.
本发明公开了一种易清洁釉料、卫生洁具及其制备方法，涉及卫生洁具技术领域。本发明的易清洁釉料包括以下质量份数的原料：石英粉15～22份、硅灰石8～15份、钾长石25～40份、碳酸锂3～10份和硼熔块15～30份；硼熔块的熔融温度为1050～1160℃，且按质量百分数计算，硼熔块中三氧化二硼的含量大于等于10％。本发明的易清洁釉料能显著降低釉面的粗糙度，使釉面光滑且平整度高，使釉面不易吸污，具备优异的易清洁效果，解决了现有易清洁釉在使用过程中仍存在容易吸污的问题。
Easy-to-clean glaze, sanitary ware and preparation method of easy-to-clean glaze
一种易清洁釉料、卫生洁具及其制备方法
BAI JINGJING (Autor:in) / YIN SHIXIN (Autor:in) / HUANG TAO (Autor:in) / ZENG SHENGJUN (Autor:in) / CHENG HAOJIAN (Autor:in) / YANG LIXIN (Autor:in) / XUE FUQIN (Autor:in)
23.02.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C03C
Chemische Zusammensetzungen für Gläser, Glasuren oder Emails
,
CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2023
Black matte glaze for sanitary ware, sanitary ware and preparation method of black matte glaze
| Europäisches Patentamt | 2024
Easy-to-clean glaze ceramic tile and preparation method thereof
| Europäisches Patentamt | 2024