The invention relates to a process formula of an isostatic pressing compact alumina material channel brick, and belongs to the field of refractory materials. The invention relates to a process formula of an isostatic pressing compact alumina material channel brick, which comprises the following components in percentage by mass: 13-17% of alumina micro powder; 28-31% of tabular corundum fine powder; 4-6% of high-quality clay fine powder; 0-1%, 34-37% of tabular corundum aggregates; 1-3% of tabular corundum granules, 13-16% of a binder; the forming process is an isostatic pressing forming process. The compact alumina material channel brick is not easy to remain pores, has high density and hardness, and is more durable; the brick forming speed of the isostatic pressing forming process is higher than that of a traditional production process, the production speed is increased, and meanwhile the product quality is greatly improved.
本发明涉及一种等静压成型致密氧化铝料道砖工艺配方，属于耐火材料领域。一种等静压成型致密氧化铝料道砖工艺配方，所述配方(质量百分比)为：氧化铝微粉，13‑17％；板状刚玉细粉，28‑31％；优质粘土细粉，4‑6％；板状刚玉粒料0‑1，34‑37％；板状刚玉粒料1‑3，13‑16％；所述成型工艺为等静压成型工艺。本发明所得致密氧化铝料道砖不易存留气孔，且密度和硬度大，更加耐用；等静压成型工艺成砖速度比传统生产工艺更快，产速增快的同时，产品质量也有大幅提高。
The invention relates to a process formula of an isostatic pressing compact alumina material channel brick, and belongs to the field of refractory materials. The invention relates to a process formula of an isostatic pressing compact alumina material channel brick, which comprises the following components in percentage by mass: 13-17% of alumina micro powder; 28-31% of tabular corundum fine powder; 4-6% of high-quality clay fine powder; 0-1%, 34-37% of tabular corundum aggregates; 1-3% of tabular corundum granules, 13-16% of a binder; the forming process is an isostatic pressing forming process. The compact alumina material channel brick is not easy to remain pores, has high density and hardness, and is more durable; the brick forming speed of the isostatic pressing forming process is higher than that of a traditional production process, the production speed is increased, and meanwhile the product quality is greatly improved.
本发明涉及一种等静压成型致密氧化铝料道砖工艺配方，属于耐火材料领域。一种等静压成型致密氧化铝料道砖工艺配方，所述配方(质量百分比)为：氧化铝微粉，13‑17％；板状刚玉细粉，28‑31％；优质粘土细粉，4‑6％；板状刚玉粒料0‑1，34‑37％；板状刚玉粒料1‑3，13‑16％；所述成型工艺为等静压成型工艺。本发明所得致密氧化铝料道砖不易存留气孔，且密度和硬度大，更加耐用；等静压成型工艺成砖速度比传统生产工艺更快，产速增快的同时，产品质量也有大幅提高。
Process formula of isostatic pressing compact alumina material channel brick
一种等静压成型致密氧化铝料道砖工艺配方
29.03.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Technological formula of material basin for isostatic pressing formed glass feeding channel
| Europäisches Patentamt | 2024
HOT ISOSTATIC PRESSING DEVICE AND ISOSTATIC PRESSING PROCESSING METHOD
| Europäisches Patentamt | 2021
Rubber isostatic pressing and cold isostatic pressing of metal powder
| British Library Online Contents | 2004
| British Library Online Contents | 1999
Formula and production process of medium-high alumina brick
| Europäisches Patentamt | 2022