Environment-friendly soft porcelain based on straw and fly ash and preparation method of environment-friendly soft porcelain
The invention discloses environment-friendly soft porcelain based on straw and fly ash and a preparation method of the environment-friendly soft porcelain, and belongs to the field of novel building decoration materials. The technical problems that existing soft porcelain is prone to cracking and poor in heat preservation performance are solved. According to the technical scheme, the environment-friendly soft porcelain is prepared from the following raw materials in parts by weight: 10-15 parts of straw, 8-10 parts of fly ash, 1-2 parts of fumed silica, 25-35 parts of a water-based emulsion, 14-22 parts of quartz sand, 6-15 parts of a cellulose solution, 15-25 parts of white cement and 1 part of a defoaming agent. The invention has the following beneficial effects: through mutual cooperation of straw, fly ash and fumed silica, the material has the advantages of good flexibility and good thermal insulation property, and realizes resource utilization of industrial and agricultural solid wastes of straw and fly ash.
本发明公开了一种基于秸秆和粉煤灰的环保型软瓷及其制备方法，属于新型建筑装饰材料领域。解决了现有软瓷容易开裂且保温性不佳的技术问题。其技术方案为：该环保型软瓷，由如下重量份的原料制备而成：10～15份秸秆、8～10份粉煤灰、1～2份气相白炭黑、25～35份水性乳液、14～22份石英砂、6～15份纤维素溶液、15～25份白水泥以及1份消泡剂。本发明的有益效果为：通过秸秆、粉煤灰和气相白炭黑相互配合，具有柔韧性好、保温性佳的优点，实现秸秆和粉煤灰工农业固废的资源化利用。
Environment-friendly soft porcelain based on straw and fly ash and preparation method of environment-friendly soft porcelain
The invention discloses environment-friendly soft porcelain based on straw and fly ash and a preparation method of the environment-friendly soft porcelain, and belongs to the field of novel building decoration materials. The technical problems that existing soft porcelain is prone to cracking and poor in heat preservation performance are solved. According to the technical scheme, the environment-friendly soft porcelain is prepared from the following raw materials in parts by weight: 10-15 parts of straw, 8-10 parts of fly ash, 1-2 parts of fumed silica, 25-35 parts of a water-based emulsion, 14-22 parts of quartz sand, 6-15 parts of a cellulose solution, 15-25 parts of white cement and 1 part of a defoaming agent. The invention has the following beneficial effects: through mutual cooperation of straw, fly ash and fumed silica, the material has the advantages of good flexibility and good thermal insulation property, and realizes resource utilization of industrial and agricultural solid wastes of straw and fly ash.
本发明公开了一种基于秸秆和粉煤灰的环保型软瓷及其制备方法，属于新型建筑装饰材料领域。解决了现有软瓷容易开裂且保温性不佳的技术问题。其技术方案为：该环保型软瓷，由如下重量份的原料制备而成：10～15份秸秆、8～10份粉煤灰、1～2份气相白炭黑、25～35份水性乳液、14～22份石英砂、6～15份纤维素溶液、15～25份白水泥以及1份消泡剂。本发明的有益效果为：通过秸秆、粉煤灰和气相白炭黑相互配合，具有柔韧性好、保温性佳的优点，实现秸秆和粉煤灰工农业固废的资源化利用。
Environment-friendly soft porcelain based on straw and fly ash and preparation method of environment-friendly soft porcelain
一种基于秸秆和粉煤灰的环保型软瓷及其制备方法
LI WENBIN (Autor:in) / ZHU XITING (Autor:in) / LU HONGBIN (Autor:in) / WANG CUNXIN (Autor:in) / BIN DUAN (Autor:in) / YANG BEIBEI (Autor:in) / TANG WEI (Autor:in)
06.08.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2015