The invention discloses an acid and alkali resistant glaze paste for false teeth and a preparation method of the acid and alkali resistant glaze paste. 10-20% of aluminum oxide; 15 to 25% of zirconium oxide; 2-5% of titanium oxide; 1-3% of magnesium oxide; 3-5% of calcium oxide; 1-3% of potassium oxide; and then, the glaze paste can be prepared and used in a manner of material selection, mixing, melting, cooling, crushing, screening, pulping, coating and sintering. The invention relates to the technical field of false tooth glaze paste, and the false tooth glaze paste has the characteristic of excellent acid and alkali resistance through excellent proportioning and preparation mode.
本发明公开了一种耐酸碱的假牙用釉膏及其制备方法，其釉膏的配比为，硅酸盐：40‑60％；氧化铝：10‑20％；氧化锆：15‑25％；氧化钛：2‑5％；氧化镁：1‑3％；氧化钙：3‑5％；氧化钾：1‑3％；氧化钠：1‑3％，之后，釉膏可通过选料‑混合‑熔融‑冷却‑粉碎‑筛分‑制浆‑涂敷、烧结的方式制备和使用。本发明涉及假牙釉膏的技术领域，其通过优异的配比和制备方式，使其具有耐酸碱性能优异的特点。
The invention discloses an acid and alkali resistant glaze paste for false teeth and a preparation method of the acid and alkali resistant glaze paste. 10-20% of aluminum oxide; 15 to 25% of zirconium oxide; 2-5% of titanium oxide; 1-3% of magnesium oxide; 3-5% of calcium oxide; 1-3% of potassium oxide; and then, the glaze paste can be prepared and used in a manner of material selection, mixing, melting, cooling, crushing, screening, pulping, coating and sintering. The invention relates to the technical field of false tooth glaze paste, and the false tooth glaze paste has the characteristic of excellent acid and alkali resistance through excellent proportioning and preparation mode.
本发明公开了一种耐酸碱的假牙用釉膏及其制备方法，其釉膏的配比为，硅酸盐：40‑60％；氧化铝：10‑20％；氧化锆：15‑25％；氧化钛：2‑5％；氧化镁：1‑3％；氧化钙：3‑5％；氧化钾：1‑3％；氧化钠：1‑3％，之后，釉膏可通过选料‑混合‑熔融‑冷却‑粉碎‑筛分‑制浆‑涂敷、烧结的方式制备和使用。本发明涉及假牙釉膏的技术领域，其通过优异的配比和制备方式，使其具有耐酸碱性能优异的特点。
Artificial tooth glaze paste with excellent acid and alkali resistance and preparation method thereof
一种耐酸碱性能优异的假牙用釉膏及其制备方法
TANG JIE (Autor:in)
27.09.2024
Patent
Elektronische Ressource
Chinesisch
Ceramic glaze with strong acid and alkali resistance and preparation method thereof
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2020
Art glaze with high glaze surface hardness and preparation method thereof
| Europäisches Patentamt | 2021
White glaze ceramic product with black ground glaze and preparation method thereof
| Europäisches Patentamt | 2020
High-wear-resistance polished glaze material and preparation method thereof
| Europäisches Patentamt | 2020