Glaze material with orange peel texture, ceramic product containing glaze material and preparation method of glaze material
The invention discloses a glaze material with orange peel texture. The glaze material is prepared from the following components in parts by mass (%): 38-50 parts of feldspar powder, 14-18 parts of kaolin, 8-10 parts of calcite, 8-10 parts of talcum powder, 4-6 parts of aluminum powder, 4-6 parts of low-temperature frit and 9-11 parts of pigment, the invention further provides a preparation method of the glazed ceramic product containing the orange peel texture, and the preparation method comprises the following operation steps: S1, uniformly mixing the glaze materials, putting the mixture into ball milling equipment for ball milling, and sieving the obtained glaze slip to obtain final glaze slip; s2, spraying final glaze slip on the ceramic green body by adopting a pneumatic spray gun, spraying the glaze surface effect into particles, drying and feeding into a kiln; s3, after firing and heat preservation are conducted for a period of time, the glazed ceramic product with the orange peel texture can be prepared. The invention further provides a glazed ceramic product containing the orange peel texture. The raw materials are common, the material cost is low, batch production can be achieved through an existing roller kiln, the preparation method is simple, the production cost is low, and the glaze color effect is simulated and natural.
本申请公开了一种有桔皮纹理的釉面材料，按质量份数（%）计包括如下组分：长石粉38～50，高岭土14～18，方解石8～10，滑石粉8～10，铝粉4～6，低温熔块4～6，色料9～11；本申请还提供一种含有桔皮纹理的釉面陶瓷制品的制备方法，包括如下操作步骤：S1、将上述的釉面材料混合均匀，放入球磨设备中进行球磨，所得釉浆过筛，获得最终釉浆；S2、采用气动喷枪向陶瓷生坯上喷涂最终釉浆，釉面效果喷成颗粒状，干燥后入窑；S3、经过一段时间的烧成及保温后，即可制得含有桔皮纹理的釉面陶瓷制品；本申请还提供一种含有桔皮纹理的釉面陶瓷制品。本申请采用的原材料普通，材料成本较低，并可使用现有辊道窑炉批量生产，制备方法简单，生产成本低，釉面颜色效果仿真自然。
Glaze material with orange peel texture, ceramic product containing glaze material and preparation method of glaze material
The invention discloses a glaze material with orange peel texture. The glaze material is prepared from the following components in parts by mass (%): 38-50 parts of feldspar powder, 14-18 parts of kaolin, 8-10 parts of calcite, 8-10 parts of talcum powder, 4-6 parts of aluminum powder, 4-6 parts of low-temperature frit and 9-11 parts of pigment, the invention further provides a preparation method of the glazed ceramic product containing the orange peel texture, and the preparation method comprises the following operation steps: S1, uniformly mixing the glaze materials, putting the mixture into ball milling equipment for ball milling, and sieving the obtained glaze slip to obtain final glaze slip; s2, spraying final glaze slip on the ceramic green body by adopting a pneumatic spray gun, spraying the glaze surface effect into particles, drying and feeding into a kiln; s3, after firing and heat preservation are conducted for a period of time, the glazed ceramic product with the orange peel texture can be prepared. The invention further provides a glazed ceramic product containing the orange peel texture. The raw materials are common, the material cost is low, batch production can be achieved through an existing roller kiln, the preparation method is simple, the production cost is low, and the glaze color effect is simulated and natural.
本申请公开了一种有桔皮纹理的釉面材料，按质量份数（%）计包括如下组分：长石粉38～50，高岭土14～18，方解石8～10，滑石粉8～10，铝粉4～6，低温熔块4～6，色料9～11；本申请还提供一种含有桔皮纹理的釉面陶瓷制品的制备方法，包括如下操作步骤：S1、将上述的釉面材料混合均匀，放入球磨设备中进行球磨，所得釉浆过筛，获得最终釉浆；S2、采用气动喷枪向陶瓷生坯上喷涂最终釉浆，釉面效果喷成颗粒状，干燥后入窑；S3、经过一段时间的烧成及保温后，即可制得含有桔皮纹理的釉面陶瓷制品；本申请还提供一种含有桔皮纹理的釉面陶瓷制品。本申请采用的原材料普通，材料成本较低，并可使用现有辊道窑炉批量生产，制备方法简单，生产成本低，釉面颜色效果仿真自然。
Glaze material with orange peel texture, ceramic product containing glaze material and preparation method of glaze material
一种有桔皮纹理的釉面材料及含其的陶瓷制品及其制备方法
XIE QUANYING (Autor:in)
01.10.2024
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2022
Glaze material of jade glaze, ceramic tile and preparation method of ceramic tile
| Europäisches Patentamt | 2023