Ice jade porcelain pug and preparation method thereof
The invention discloses an ice jade porcelain pug and a preparation method, and relates to the technical field of ceramic pugs, the formula of the ice jade porcelain pug comprises the following components in parts by weight: 10-20 parts of Heilongjiang feldspar, 55-65 parts of fused quartz, 15-20 parts of bentonite, 5-25 parts of glaze quartz, 5-15 parts of tea spar and 0.1-0.2 part of yttrium oxide, the high-temperature glass phase of the fused quartz, the tea spar and the rare earth yttrium oxide are subjected to a reaction at 1270-1330 DEG C, and the raw materials are added into the raw materials to prepare the ice jade porcelain pug. And lattice defects of the fused quartz are filled, so that a ceramic product prepared from the pug with the formula has better light transmittance performance.
本发明公开了一种冰种玉瓷泥料以及制备方法，涉及陶瓷泥料技术领域，按重量份数计，其配方包括黑龙江长石10~20份，熔融石英55~65份，膨润土15~20份，釉用石英5~25份，茶晶石5~15份，氧化钇0.1~0.2份，利用熔融石英高温玻璃相、茶晶石、稀土氧化钇1270~1330℃反应，使熔融石英的晶格缺陷得以填补，从而使得用该配方的泥料制得的陶瓷产品的透光性能更好。
Ice jade porcelain pug and preparation method thereof
The invention discloses an ice jade porcelain pug and a preparation method, and relates to the technical field of ceramic pugs, the formula of the ice jade porcelain pug comprises the following components in parts by weight: 10-20 parts of Heilongjiang feldspar, 55-65 parts of fused quartz, 15-20 parts of bentonite, 5-25 parts of glaze quartz, 5-15 parts of tea spar and 0.1-0.2 part of yttrium oxide, the high-temperature glass phase of the fused quartz, the tea spar and the rare earth yttrium oxide are subjected to a reaction at 1270-1330 DEG C, and the raw materials are added into the raw materials to prepare the ice jade porcelain pug. And lattice defects of the fused quartz are filled, so that a ceramic product prepared from the pug with the formula has better light transmittance performance.
本发明公开了一种冰种玉瓷泥料以及制备方法，涉及陶瓷泥料技术领域，按重量份数计，其配方包括黑龙江长石10~20份，熔融石英55~65份，膨润土15~20份，釉用石英5~25份，茶晶石5~15份，氧化钇0.1~0.2份，利用熔融石英高温玻璃相、茶晶石、稀土氧化钇1270~1330℃反应，使熔融石英的晶格缺陷得以填补，从而使得用该配方的泥料制得的陶瓷产品的透光性能更好。
Ice jade porcelain pug and preparation method thereof
一种冰种玉瓷泥料以及制备方法
LIN SINAN (Autor:in) / CAI SHUQIANG (Autor:in) / ZHAO HEHAO (Autor:in)
15.10.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Taishan jade porcelain and preparation method thereof
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2022
High-strength jade porcelain pug and preparation method thereof
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2015
Jade-imitated soft porcelain and manufacturing method thereof
| Europäisches Patentamt | 2022