Colored glaze and firing method thereof
The brown glaze is prepared from the following components in percentage by weight: 25.2 percent to 30.8 percent of potassium feldspar, 8.1 percent to 9.9 percent of quartz powder, 8.1 percent to 9.9 percent of calcium carbonate, 4.5 percent to 5.5 percent of black clay, 4.5 percent to 5.5 percent of wood ash, 5.4 percent to 6.6 percent of yellow sand soil, 8.1 percent to 9.9 percent of white clay, 2.7 percent to 3.3 percent of soybean stalk ash, 2.7 percent to 3.3 percent of agate, 2.7 percent to 3.3 percent of zirconium silicate, 2.7 percent to 3.3 percent of titanium oxide, 0.9 percent to 1.1 percent of blue-and-white material, 5.4 percent to 6.6 percent of Wuhua soil, 2.7 percent to 3.3 percent of rice washing water, 2.7 percent to 3.3 percent of zinc oxide, 0.72 percent to 0.88 percent of sodium silicate and the balance of water. And 2.88%-3.52% of glass powder. The brown glaze has the advantages that the brown glaze is not only rich and bright in color layer, but also colorful and crystal clear.
本发明公开了一种玄彩釉及其烧制方法，其中的玄彩釉由以下重量百分数的组分组成：钾长石25.2～30.8％，石英粉8.1～9.9％，碳酸钙8.1～9.9％，黑泥4.5～5.5％，柴灰4.5～5.5％，黄沙土5.4～6.6％，白泥土8.1～9.9％，黄豆杆灰2.7～3.3％，玛瑙2.7～3.3％，硅酸锆2.7～3.3％，氧化钛2.7～3.3％，青花料0.9～1.1％，五花土5.4～6.6％，淘米水2.7～3.3％，氧化锌2.7～3.3％，硅酸钠0.72～0.88％，玻璃粉2.88～3.52％。本发明的优点在于：本发明的玄彩釉釉色不仅色彩层次够丰富、鲜亮，而且五彩斑斓，晶莹剔透。
Colored glaze and firing method thereof
The brown glaze is prepared from the following components in percentage by weight: 25.2 percent to 30.8 percent of potassium feldspar, 8.1 percent to 9.9 percent of quartz powder, 8.1 percent to 9.9 percent of calcium carbonate, 4.5 percent to 5.5 percent of black clay, 4.5 percent to 5.5 percent of wood ash, 5.4 percent to 6.6 percent of yellow sand soil, 8.1 percent to 9.9 percent of white clay, 2.7 percent to 3.3 percent of soybean stalk ash, 2.7 percent to 3.3 percent of agate, 2.7 percent to 3.3 percent of zirconium silicate, 2.7 percent to 3.3 percent of titanium oxide, 0.9 percent to 1.1 percent of blue-and-white material, 5.4 percent to 6.6 percent of Wuhua soil, 2.7 percent to 3.3 percent of rice washing water, 2.7 percent to 3.3 percent of zinc oxide, 0.72 percent to 0.88 percent of sodium silicate and the balance of water. And 2.88%-3.52% of glass powder. The brown glaze has the advantages that the brown glaze is not only rich and bright in color layer, but also colorful and crystal clear.
本发明公开了一种玄彩釉及其烧制方法，其中的玄彩釉由以下重量百分数的组分组成：钾长石25.2～30.8％，石英粉8.1～9.9％，碳酸钙8.1～9.9％，黑泥4.5～5.5％，柴灰4.5～5.5％，黄沙土5.4～6.6％，白泥土8.1～9.9％，黄豆杆灰2.7～3.3％，玛瑙2.7～3.3％，硅酸锆2.7～3.3％，氧化钛2.7～3.3％，青花料0.9～1.1％，五花土5.4～6.6％，淘米水2.7～3.3％，氧化锌2.7～3.3％，硅酸钠0.72～0.88％，玻璃粉2.88～3.52％。本发明的优点在于：本发明的玄彩釉釉色不仅色彩层次够丰富、鲜亮，而且五彩斑斓，晶莹剔透。
Colored glaze and firing method thereof
一种玄彩釉及其烧制方法
SHU WENZHAO (Autor:in) / LIU XI (Autor:in)
19.11.2024
Patent