Ceramic green body prepared from high-content tailings, high-strength ceramic tile and preparation methods of ceramic green body and high-strength ceramic tile
The invention provides a ceramic green body prepared from high-content tailings, a high-strength ceramic tile and a preparation method. The ceramic green body is prepared from the following raw materials in parts by weight: 20 to 30 parts of red mud, 0 to 8 parts of bentonite, 65 to 70 parts of vanadium-titanium slag, 0 to 10 parts of ball clay and 0.3 to 0.5 part of green body dispergator. According to the invention, two low-quality raw materials of red mud and vanadium-titanium slag are doped in a large amount and are reasonably proportioned to replace a traditional high-aluminum enhanced green body formula system, so that the firing temperature of a ceramic product is greatly reduced, the firing period is shortened, the huge harm of stacking of red mud and vanadium-titanium slag to natural ecology and environment is solved, and the production cost is reduced. And meanwhile, the red mud and the vanadium-titanium slag are utilized more reasonably.
本发明提供了一种高掺量尾渣制备的陶瓷坯体、高强陶瓷砖及制备方法，所述陶瓷坯体的原料按重量份计包括：赤泥20‑30份、膨润土0‑8份、钒钛渣65‑70份、球土0‑10份、坯体解胶剂0.3‑0.5份。本发明通过大量掺入赤泥和钒钛渣这两种低质原料，经合理配比，取代传统的采用高铝增强的坯体配方体系，大幅降低了陶瓷产品的烧成温度并缩短了烧成周期，不仅解决了赤泥、钒钛渣的堆放给自然生态及环境带来的巨大危害，同时更为合理地利用了赤泥和钒钛渣。
Ceramic green body prepared from high-content tailings, high-strength ceramic tile and preparation methods of ceramic green body and high-strength ceramic tile
The invention provides a ceramic green body prepared from high-content tailings, a high-strength ceramic tile and a preparation method. The ceramic green body is prepared from the following raw materials in parts by weight: 20 to 30 parts of red mud, 0 to 8 parts of bentonite, 65 to 70 parts of vanadium-titanium slag, 0 to 10 parts of ball clay and 0.3 to 0.5 part of green body dispergator. According to the invention, two low-quality raw materials of red mud and vanadium-titanium slag are doped in a large amount and are reasonably proportioned to replace a traditional high-aluminum enhanced green body formula system, so that the firing temperature of a ceramic product is greatly reduced, the firing period is shortened, the huge harm of stacking of red mud and vanadium-titanium slag to natural ecology and environment is solved, and the production cost is reduced. And meanwhile, the red mud and the vanadium-titanium slag are utilized more reasonably.
本发明提供了一种高掺量尾渣制备的陶瓷坯体、高强陶瓷砖及制备方法，所述陶瓷坯体的原料按重量份计包括：赤泥20‑30份、膨润土0‑8份、钒钛渣65‑70份、球土0‑10份、坯体解胶剂0.3‑0.5份。本发明通过大量掺入赤泥和钒钛渣这两种低质原料，经合理配比，取代传统的采用高铝增强的坯体配方体系，大幅降低了陶瓷产品的烧成温度并缩短了烧成周期，不仅解决了赤泥、钒钛渣的堆放给自然生态及环境带来的巨大危害，同时更为合理地利用了赤泥和钒钛渣。
Ceramic green body prepared from high-content tailings, high-strength ceramic tile and preparation methods of ceramic green body and high-strength ceramic tile
一种高掺量尾渣制备的陶瓷坯体、高强陶瓷砖及制备方法
YU HAILONG (Autor:in) / XU LEI (Autor:in) / LIN KEHUI (Autor:in) / HUANG CAIWEI (Autor:in) / HE CHENGXIU (Autor:in) / WANG YONGQIANG (Autor:in) / YANG HANLING (Autor:in) / LIU RENSONG (Autor:in) / DENG JIANGWEN (Autor:in)
03.01.2025
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2025