Transparent glaze and preparation method thereof, and ceramic tile and preparation method thereof
The invention discloses transparent glaze and a preparation method thereof as well as a ceramic tile and a preparation method thereof, and relates to the technical field of ceramics. In the chemical composition of the transparent glaze, the mass ratio of SiO2 to Al2O3 is (3.1-4.2): 1, and the transparent glaze contains 95 wt%-97 wt% of a glass phase and 3 wt%-5 wt% of a corundum crystal phase. According to the transparent glaze, 95 wt%-97 wt% of a glass phase and 3 wt%-5 wt% of a corundum crystal phase are formed by adjusting the content and the proportion of aluminum oxide and silicon oxide, the glass phase can enable the transparent glaze to have high transparency and enable dark ceramic tile patterns and textures to be fully displayed, and the corundum crystal phase can enable the transparent glaze to have good abrasion resistance. The requirement of the brick surface on wear resistance is met.
本发明公开了透明釉及其制备方法、陶瓷砖及其制备方法，涉及陶瓷技术领域。该透明釉的化学组成中，SiO2与Al2O3的质量比为(3.1~4.2):1，并且所述透明釉中含有95wt%~97wt%玻璃相和3wt%~5wt%刚玉晶相。该透明釉通过调整氧化铝及氧化硅的含量及配比，使透明釉形成95wt%~97wt%玻璃相和3wt%~5wt%刚玉晶相，该玻璃相可使透明釉具有较高的透明度，可使深色陶瓷砖图案纹理得以充分展示，而所述刚玉晶相可使透明釉具有较好的耐磨性，满足砖面对耐磨性的要求。
Transparent glaze and preparation method thereof, and ceramic tile and preparation method thereof
The invention discloses transparent glaze and a preparation method thereof as well as a ceramic tile and a preparation method thereof, and relates to the technical field of ceramics. In the chemical composition of the transparent glaze, the mass ratio of SiO2 to Al2O3 is (3.1-4.2): 1, and the transparent glaze contains 95 wt%-97 wt% of a glass phase and 3 wt%-5 wt% of a corundum crystal phase. According to the transparent glaze, 95 wt%-97 wt% of a glass phase and 3 wt%-5 wt% of a corundum crystal phase are formed by adjusting the content and the proportion of aluminum oxide and silicon oxide, the glass phase can enable the transparent glaze to have high transparency and enable dark ceramic tile patterns and textures to be fully displayed, and the corundum crystal phase can enable the transparent glaze to have good abrasion resistance. The requirement of the brick surface on wear resistance is met.
本发明公开了透明釉及其制备方法、陶瓷砖及其制备方法，涉及陶瓷技术领域。该透明釉的化学组成中，SiO2与Al2O3的质量比为(3.1~4.2):1，并且所述透明釉中含有95wt%~97wt%玻璃相和3wt%~5wt%刚玉晶相。该透明釉通过调整氧化铝及氧化硅的含量及配比，使透明釉形成95wt%~97wt%玻璃相和3wt%~5wt%刚玉晶相，该玻璃相可使透明釉具有较高的透明度，可使深色陶瓷砖图案纹理得以充分展示，而所述刚玉晶相可使透明釉具有较好的耐磨性，满足砖面对耐磨性的要求。
Transparent glaze and preparation method thereof, and ceramic tile and preparation method thereof
透明釉及其制备方法、陶瓷砖及其制备方法
CHEN ZHANGWU (Autor:in) / TANG QIUYUN (Autor:in) / LIANG GUOYOU (Autor:in) / ZENG XU (Autor:in) / PENG JUN (Autor:in) / MA YUANYUAN (Autor:in) / LIU JUNSHENG (Autor:in) / XIONG YUNSHENG (Autor:in)
10.01.2025
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2021
Protective glaze, preparation method thereof and ceramic tile
| Europäisches Patentamt | 2025
Pearl glaze ink, pearl glaze ceramic tile and preparation method thereof
| Europäisches Patentamt | 2021
Mulberry glaze ceramic tile and preparation method thereof
| Europäisches Patentamt | 2024
Plain rock glaze, preparation method thereof and ceramic tile
| Europäisches Patentamt | 2023