CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a cement composition containing lime stone, blast furnace slag and, if needed, chlorine bypass dust suppressing carbon dioxide discharge amount and capable of suppressing adiabatic temperature rise amount while maintaining and enhancing strength development and a manufacturing method therefor.SOLUTION: Thee is provided a cement composition containing cement clinker, gypsum, lime stone and blast furnace slag with the lime stone amount of 1 to 10 mass%, the blast furnace slag amount of 30 mass% to 69 mass%, the total of the lime stone and the blast furnace slag of 40 mass% to 70 mass% and the chlorine ion amount of 0.02 to 0.1 mass% based on the total mass of the cement composition. There is provided a manufacturing method of the cement composition including a process for mixing and pulverizing the cement clinker, the gypsum, the lime stone, the blast furnace slag and chlorine bypass dust so that the total amount of the lime stone and the blast furnace slag of 40 mass% to 70 mass% based on the total mass of the cement composition, where the chloride ion amount in the chlorine bypass dust is 2 to 35 mass%.SELECTED DRAWING: Figure 1
【課題】二酸化炭素排出量を抑制させ、強度発現性を維持・向上させつつ、断熱温度上昇量を抑制させ得る、石灰石、高炉スラグ及び必要に応じて塩素バイパスダストを含むセメント組成物及びその製造方法を提供する。【解決手段】セメントクリンカーと、石膏と、石灰石と、高炉スラグとを含むセメント組成物であって、セメント組成物の全質量を基準として、石灰石量が１〜１０質量％、高炉スラグ量が３０質量％以上６９質量％以下、石灰石と高炉スラグの合量が４０質量％以上７０質量％以下であり、塩化物イオン量が０．０２〜０．１質量％であることを特徴とするセメント組成物である。セメント組成物の全質量を基準として、石灰石と高炉スラグの合量が４０質量％以上７０質量％以下となるように、セメントクリンカー、石膏、石灰石、高炉スラグ及び塩素バイパスダストを混合粉砕する工程を含み、塩素バイパスダスト中の塩化物イオン量が２〜３５質量％である、セメント組成物の製造方法である。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a cement composition containing lime stone, blast furnace slag and, if needed, chlorine bypass dust suppressing carbon dioxide discharge amount and capable of suppressing adiabatic temperature rise amount while maintaining and enhancing strength development and a manufacturing method therefor.SOLUTION: Thee is provided a cement composition containing cement clinker, gypsum, lime stone and blast furnace slag with the lime stone amount of 1 to 10 mass%, the blast furnace slag amount of 30 mass% to 69 mass%, the total of the lime stone and the blast furnace slag of 40 mass% to 70 mass% and the chlorine ion amount of 0.02 to 0.1 mass% based on the total mass of the cement composition. There is provided a manufacturing method of the cement composition including a process for mixing and pulverizing the cement clinker, the gypsum, the lime stone, the blast furnace slag and chlorine bypass dust so that the total amount of the lime stone and the blast furnace slag of 40 mass% to 70 mass% based on the total mass of the cement composition, where the chloride ion amount in the chlorine bypass dust is 2 to 35 mass%.SELECTED DRAWING: Figure 1
【課題】二酸化炭素排出量を抑制させ、強度発現性を維持・向上させつつ、断熱温度上昇量を抑制させ得る、石灰石、高炉スラグ及び必要に応じて塩素バイパスダストを含むセメント組成物及びその製造方法を提供する。【解決手段】セメントクリンカーと、石膏と、石灰石と、高炉スラグとを含むセメント組成物であって、セメント組成物の全質量を基準として、石灰石量が１〜１０質量％、高炉スラグ量が３０質量％以上６９質量％以下、石灰石と高炉スラグの合量が４０質量％以上７０質量％以下であり、塩化物イオン量が０．０２〜０．１質量％であることを特徴とするセメント組成物である。セメント組成物の全質量を基準として、石灰石と高炉スラグの合量が４０質量％以上７０質量％以下となるように、セメントクリンカー、石膏、石灰石、高炉スラグ及び塩素バイパスダストを混合粉砕する工程を含み、塩素バイパスダスト中の塩化物イオン量が２〜３５質量％である、セメント組成物の製造方法である。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
セメント組成物及びその製造方法
DENKOUCHI JIN (Autor:in) / ITO TAKAYASU (Autor:in) / SAWABE NORIHIKO (Autor:in) / MATSUMOTO MASAHIRO (Autor:in)
23.05.2016
Patent
Elektronische Ressource
Japanisch