PROBLEM TO BE SOLVED: To provide high strength spray concrete having all of properties capable of inhibiting flash setting such as a hindrance with regard to building, adding excellent adhesiveness during spray, increasing strength extremely quickly after spray and forming a sprayed article having extremely high strength by short time material age.SOLUTION: There is provided high strength spray concrete made by adding a powder additive containing a ground product of clinker of calcium aluminate having a content molar ratio of CaO and AlO(CaO/AlO) of 1.8 to 2.5 with a vitrification percentage of 90% or more containing silicon, magnesium and titanium of SiO; 4 to 6 mass%, MgO; 0.75 to 0.95 mass% and TiO; 0.8 to 1.3 mass% in terms of oxide, sodium aluminate and anhydrous gypsum to a cement composition containing 100 pts.mass of cement and 5 to 12 pts.mass of anhydrous gypsum, by an addition amount of 5 to 15 pts.mass based on 100 pts.mass of the cement content in the cement composition.SELECTED DRAWING: None
【課題】 施工に関して支障をきたすほどの瞬結化を抑制でき、一方で、吹付の際に優れた付着性を付与でき、吹付後は著しく早く強度が増加し、短時間材齢での強度が格段に高い吹付物を形成できるという特性を全て具備した高強度吹付コンクリートを提供する。【解決手段】 セメント１００質量部及び無水石膏５〜１２質量部を含有するセメント組成物に、ガラス化率９０％以上でＣａＯとＡｌ2Ｏ3の含有モル比（ＣａＯ／Ａｌ2Ｏ3）が１．８〜２．５のカルシウムアルミネートのクリンカであって、珪素、マグネシウム及びチタンを酸化物換算で、ＳｉＯ2；４〜６質量％、ＭｇＯ；０．７５〜０．９５質量％及びＴｉＯ2；０．８〜１．３質量％含有するクリンカの粉砕物、アルミン酸ナトリウム及び無水石膏を含有する粉体混和剤を、前記セメント組成物中のセメント含有量１００質量部に対する添加量が５〜１５質量部となるよう添加添加してなる高強度吹付コンクリート。【選択図】 なし
PROBLEM TO BE SOLVED: To provide high strength spray concrete having all of properties capable of inhibiting flash setting such as a hindrance with regard to building, adding excellent adhesiveness during spray, increasing strength extremely quickly after spray and forming a sprayed article having extremely high strength by short time material age.SOLUTION: There is provided high strength spray concrete made by adding a powder additive containing a ground product of clinker of calcium aluminate having a content molar ratio of CaO and AlO(CaO/AlO) of 1.8 to 2.5 with a vitrification percentage of 90% or more containing silicon, magnesium and titanium of SiO; 4 to 6 mass%, MgO; 0.75 to 0.95 mass% and TiO; 0.8 to 1.3 mass% in terms of oxide, sodium aluminate and anhydrous gypsum to a cement composition containing 100 pts.mass of cement and 5 to 12 pts.mass of anhydrous gypsum, by an addition amount of 5 to 15 pts.mass based on 100 pts.mass of the cement content in the cement composition.SELECTED DRAWING: None
【課題】 施工に関して支障をきたすほどの瞬結化を抑制でき、一方で、吹付の際に優れた付着性を付与でき、吹付後は著しく早く強度が増加し、短時間材齢での強度が格段に高い吹付物を形成できるという特性を全て具備した高強度吹付コンクリートを提供する。【解決手段】 セメント１００質量部及び無水石膏５〜１２質量部を含有するセメント組成物に、ガラス化率９０％以上でＣａＯとＡｌ2Ｏ3の含有モル比（ＣａＯ／Ａｌ2Ｏ3）が１．８〜２．５のカルシウムアルミネートのクリンカであって、珪素、マグネシウム及びチタンを酸化物換算で、ＳｉＯ2；４〜６質量％、ＭｇＯ；０．７５〜０．９５質量％及びＴｉＯ2；０．８〜１．３質量％含有するクリンカの粉砕物、アルミン酸ナトリウム及び無水石膏を含有する粉体混和剤を、前記セメント組成物中のセメント含有量１００質量部に対する添加量が５〜１５質量部となるよう添加添加してなる高強度吹付コンクリート。【選択図】 なし
HIGH STRENGTH SPRAY CONCRETE
高強度吹付コンクリート
HANEI YOSHIHISA (Autor:in)
11.07.2016
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
Concrete strength increased by spray irrigation
| Engineering Index Backfile | 1933
High strength, density controlled cold fusion concrete cementitious spray applied fireproofing
| Europäisches Patentamt | 2018
High strength, density controlled cold fusion concrete cementitious spray applied fireproofing
| Europäisches Patentamt | 2017
High strength, density controlled cold fusion concrete cementitious spray applied fireproofing
| Europäisches Patentamt | 2017
HIGH STRENGTH, DENSITY CONTROLLED COLD FUSION CONCRETE CEMENTITIOUS SPRAY APPLIED FIREPROOFING
| Europäisches Patentamt | 2018