SLAG PRODUCT RAW MATERIAL AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a high quality slag product raw material capable of replacement of natural rock containing a steel slag as a raw material and a manufacturing method of the slag product raw material capable of manufacturing the same with productivity.SOLUTION: There is provided a slag product raw material containing a steel slag as a raw material, having a chemical composition having slag basicity (CaO mass/SiOmass) of 1.5 or more and AlOconcentration of 8 mass% or less and uniaxial compressive strength measured according to JIS A 1132 of 50 MPa or more. The raw material is manufactured by treating the molten steel slag by reduction and modification to have slag basicity (CaO mass/SiOmass) of 1.5 or more and AlOconcentration of 8 mass% or less, and setting a temperature of the molten slag in a container at removal completion at a temperature that a solid phase percentage of the molten slag is 30% +100°C or more when the molten steel slag is removed from a treatment furnace and solidified in the container.SELECTED DRAWING: Figure 1
【課題】製鋼スラグを原料とする天然石代替とすることが可能な高品質のスラグ製品素材、およびそれを生産性をもって製造することができる、スラグ製品素材の製造方法を提供する。【解決手段】製鋼スラグを原料とするスラグ製品素材であって、スラグ塩基度（ＣａＯ質量／ＳｉＯ2質量）が１．５以上、Ａｌ2Ｏ3濃度が８質量％以下の化学組成を有すると共に、ＪＩＳ Ａ １１３２に準拠して測定される一軸圧縮強度が５０ＭＰa以上であるスラグ製品素材である。その素材を、溶融した製鋼スラグを還元および改質処理してスラグ塩基度（ＣａＯ質量／ＳｉＯ2質量）を１．５以上、Ａｌ2Ｏ3濃度が８％以下とし、それを処理炉から排滓して容器内で凝固させる際に、排滓完了時の容器内の溶融スラグの温度が、前記溶融スラグの固相率が質量比率で３０％になる温度＋１００℃以上となるように、当該溶融スラグの温度を調整して排滓することによって製造する。【選択図】図１
SLAG PRODUCT RAW MATERIAL AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a high quality slag product raw material capable of replacement of natural rock containing a steel slag as a raw material and a manufacturing method of the slag product raw material capable of manufacturing the same with productivity.SOLUTION: There is provided a slag product raw material containing a steel slag as a raw material, having a chemical composition having slag basicity (CaO mass/SiOmass) of 1.5 or more and AlOconcentration of 8 mass% or less and uniaxial compressive strength measured according to JIS A 1132 of 50 MPa or more. The raw material is manufactured by treating the molten steel slag by reduction and modification to have slag basicity (CaO mass/SiOmass) of 1.5 or more and AlOconcentration of 8 mass% or less, and setting a temperature of the molten slag in a container at removal completion at a temperature that a solid phase percentage of the molten slag is 30% +100°C or more when the molten steel slag is removed from a treatment furnace and solidified in the container.SELECTED DRAWING: Figure 1
【課題】製鋼スラグを原料とする天然石代替とすることが可能な高品質のスラグ製品素材、およびそれを生産性をもって製造することができる、スラグ製品素材の製造方法を提供する。【解決手段】製鋼スラグを原料とするスラグ製品素材であって、スラグ塩基度（ＣａＯ質量／ＳｉＯ2質量）が１．５以上、Ａｌ2Ｏ3濃度が８質量％以下の化学組成を有すると共に、ＪＩＳ Ａ １１３２に準拠して測定される一軸圧縮強度が５０ＭＰa以上であるスラグ製品素材である。その素材を、溶融した製鋼スラグを還元および改質処理してスラグ塩基度（ＣａＯ質量／ＳｉＯ2質量）を１．５以上、Ａｌ2Ｏ3濃度が８％以下とし、それを処理炉から排滓して容器内で凝固させる際に、排滓完了時の容器内の溶融スラグの温度が、前記溶融スラグの固相率が質量比率で３０％になる温度＋１００℃以上となるように、当該溶融スラグの温度を調整して排滓することによって製造する。【選択図】図１
SLAG PRODUCT RAW MATERIAL AND MANUFACTURING METHOD THEREFOR
スラグ製品素材およびその製造方法
HIRATA HIROSHI (Autor:in) / HARADA TOSHIYA (Autor:in)
12.08.2016
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
METHOD FOR MANUFACTURING SLAG MATERIAL, AND SLAG MATERIAL
| Europäisches Patentamt | 2022
MANUFACTURING METHOD OF SLAG ROADBED MATERIAL AND ITS SLAG ROADBED MATERIAL
| Europäisches Patentamt | 2022