CORDIERITE MEMBRANE ON CORDIERITE MONOLITH
PROBLEM TO BE SOLVED: To provide an improved cordierite membrane monolith of a type in which a cordierite membrane coating is applied onto a monolith substrate formed from cordierite.SOLUTION: The membrane coating is formed from cordierite particles which have been processed to have a median particle diameter of 1-3 μm with a narrow particle size distribution suitable for forming a cordierite membrane on a cordierite monolith substrate. After the cordierite membrane is formed on the cordierite monolith substrate, the cordierite membrane monolith has a pore size of less than 1 μm. The cordierite monolith substrate may be a honeycomb monolith substrate including a plurality of inner channels having surfaces defined by porous channel walls.SELECTED DRAWING: Figure 13
【課題】コージエライトから形成されたモノリス基材上に、コージエライト膜がコーティングされたタイプの、改良されたコージエライト膜モノリスを提供する。【解決手段】コージエライトモノリス基材上にコージエライト膜を形成するのに適した狭い粒径分布を有する、１〜３μｍのメジアン粒子直径を有するように加工されたコージエライト粒子から、膜コーティングが形成される。このコージエライト膜がコージエライトモノリス基材上に形成された後、コージエライト膜モノリスは１μｍ未満の細孔径を有する。コージエライトモノリス基材は、多孔質のチャネル壁によって画成された表面を有する複数の内部チャネルを含む、ハニカムモノリス基材であってもよい。【選択図】図１３
CORDIERITE MEMBRANE ON CORDIERITE MONOLITH
PROBLEM TO BE SOLVED: To provide an improved cordierite membrane monolith of a type in which a cordierite membrane coating is applied onto a monolith substrate formed from cordierite.SOLUTION: The membrane coating is formed from cordierite particles which have been processed to have a median particle diameter of 1-3 μm with a narrow particle size distribution suitable for forming a cordierite membrane on a cordierite monolith substrate. After the cordierite membrane is formed on the cordierite monolith substrate, the cordierite membrane monolith has a pore size of less than 1 μm. The cordierite monolith substrate may be a honeycomb monolith substrate including a plurality of inner channels having surfaces defined by porous channel walls.SELECTED DRAWING: Figure 13
【課題】コージエライトから形成されたモノリス基材上に、コージエライト膜がコーティングされたタイプの、改良されたコージエライト膜モノリスを提供する。【解決手段】コージエライトモノリス基材上にコージエライト膜を形成するのに適した狭い粒径分布を有する、１〜３μｍのメジアン粒子直径を有するように加工されたコージエライト粒子から、膜コーティングが形成される。このコージエライト膜がコージエライトモノリス基材上に形成された後、コージエライト膜モノリスは１μｍ未満の細孔径を有する。コージエライトモノリス基材は、多孔質のチャネル壁によって画成された表面を有する複数の内部チャネルを含む、ハニカムモノリス基材であってもよい。【選択図】図１３
CORDIERITE MEMBRANE ON CORDIERITE MONOLITH
コージエライトモノリスにおけるコージエライト膜
JOEL E CLINTON (Autor:in) / KENNETH J DRURY (Autor:in) / GU YUNFENG (Autor:in) / MICHEL E SAUNDERS (Autor:in)
17.11.2016
Patent
Elektronische Ressource
Japanisch
CORDIERITE-BASED COMPOSITE MEMBRANE COATED ON CORDIERITE MONOLITH
| Europäisches Patentamt | 2019