SPARK PLUG
PROBLEM TO BE SOLVED: To provide a spark plug with an insulator superior in voltage-resistance performance under a high-temperature condition.SOLUTION: A spark plug comprises: an insulator including 92-96 mass% of Al components in terms of oxide. The insulator is formed by an alumina sintered body having alumina crystal phases and grain boundary phases present between the alumina crystal phases. The grain boundary phases include Si, Mg, Ba and Ca components. Supposing that their contents by mass in terms of oxide are M, M, Mand Mrespectively, and the total content thereof is Mt, the following expressions (1)-(4) are satisfied: (1) 0.17≤M/Mt≤0.47; (2) 0.005≤M/Mt≤0.07; (3) 0.29≤M/Mt≤0.77; and (4) 0.03≤M/Mt≤0.19.SELECTED DRAWING: Figure 1
【課題】 この発明は、高温下における耐電圧性能に優れた絶縁体を備えたスパークプラグを提供することを課題とする。【解決手段】 Ａｌ成分を酸化物換算で９２質量％以上９６質量％以下含む絶縁体を備えたスパークプラグであって、前記絶縁体は、アルミナ結晶と前記アルミナ結晶の結晶間に存在する粒界相とからなるアルミナ焼結体で形成され、前記粒界相は、Ｓｉ成分、Ｍｇ成分、Ｂａ成分、及びＣａ成分を含有し、酸化物換算したときの質量含有率をそれぞれＭＳｉＯ２、ＭＭｇＯ、ＭＢａＯ、及びＭＣａＯとし、これらの合計をＭｔとしたとき、下記の（１）〜（４）を満たすことを特徴とするスパークプラグ。（１）０．１７≦ＭＳｉＯ２／Ｍｔ≦０．４７（２）０．００５≦ＭＭｇＯ／Ｍｔ≦０．０７（３）０．２９≦ＭＢａＯ／Ｍｔ≦０．７７（４）０．０３≦ＭＣａＯ／Ｍｔ≦０．１９【選択図】 図１
SPARK PLUG
PROBLEM TO BE SOLVED: To provide a spark plug with an insulator superior in voltage-resistance performance under a high-temperature condition.SOLUTION: A spark plug comprises: an insulator including 92-96 mass% of Al components in terms of oxide. The insulator is formed by an alumina sintered body having alumina crystal phases and grain boundary phases present between the alumina crystal phases. The grain boundary phases include Si, Mg, Ba and Ca components. Supposing that their contents by mass in terms of oxide are M, M, Mand Mrespectively, and the total content thereof is Mt, the following expressions (1)-(4) are satisfied: (1) 0.17≤M/Mt≤0.47; (2) 0.005≤M/Mt≤0.07; (3) 0.29≤M/Mt≤0.77; and (4) 0.03≤M/Mt≤0.19.SELECTED DRAWING: Figure 1
【課題】 この発明は、高温下における耐電圧性能に優れた絶縁体を備えたスパークプラグを提供することを課題とする。【解決手段】 Ａｌ成分を酸化物換算で９２質量％以上９６質量％以下含む絶縁体を備えたスパークプラグであって、前記絶縁体は、アルミナ結晶と前記アルミナ結晶の結晶間に存在する粒界相とからなるアルミナ焼結体で形成され、前記粒界相は、Ｓｉ成分、Ｍｇ成分、Ｂａ成分、及びＣａ成分を含有し、酸化物換算したときの質量含有率をそれぞれＭＳｉＯ２、ＭＭｇＯ、ＭＢａＯ、及びＭＣａＯとし、これらの合計をＭｔとしたとき、下記の（１）〜（４）を満たすことを特徴とするスパークプラグ。（１）０．１７≦ＭＳｉＯ２／Ｍｔ≦０．４７（２）０．００５≦ＭＭｇＯ／Ｍｔ≦０．０７（３）０．２９≦ＭＢａＯ／Ｍｔ≦０．７７（４）０．０３≦ＭＣａＯ／Ｍｔ≦０．１９【選択図】 図１