POWDERY CEMENT COMPOSITION FOR PLASTERER AND MORTAR FOR PLASTERER
PROBLEM TO BE SOLVED: To provide a powdery cement composition for plasterer good in workability even without using specific limestone fine powder when used as a mortar for plasterer and good in evaluation of dripping of mortar after coating on a wall surface or the like (dripping hardness).SOLUTION: There is provided a powdery cement composition containing a clinker ground product, a limestone powder and gypsum, wherein the clinker ground product is normal Portland cement clinker ground product or high-early-strength Portland cement clinker ground product, percentage content of the limestone powder is 8 to 40 mass%, Blaine specific surface area is 4,500 cm/g or less, 90% vol.% cumulative particle diameter is 57 μm or less and 50 vol.% cumulative particle diameter is 22 μm or less.SELECTED DRAWING: None
【課題】左官用モルタルとして使用する際に、特殊な石灰石微粉末を使用しなくても、作業性が良好であり、かつ、壁面等に塗付けた後のモルタルの垂れの評価（ダレ難さ）が良好である、左官用粉末状セメント組成物を提供する。【解決手段】クリンカ粉砕物、石灰石粉末および石膏を含む左官用粉末状セメント組成物であって、クリンカ粉砕物が、普通ポルトランドセメントクリンカ粉砕物または早強ポルトランドセメントクリンカ粉砕物であり、石灰石粉末の含有率が８〜４０質量％であり、ブレーン比表面積が４，５００ｃｍ２／ｇ以下であり、９０体積％累積粒径が５７μｍ以下であり、５０体積％累積粒径が２２μｍ以下である、左官用粉末状セメント組成物。【選択図】なし
POWDERY CEMENT COMPOSITION FOR PLASTERER AND MORTAR FOR PLASTERER
PROBLEM TO BE SOLVED: To provide a powdery cement composition for plasterer good in workability even without using specific limestone fine powder when used as a mortar for plasterer and good in evaluation of dripping of mortar after coating on a wall surface or the like (dripping hardness).SOLUTION: There is provided a powdery cement composition containing a clinker ground product, a limestone powder and gypsum, wherein the clinker ground product is normal Portland cement clinker ground product or high-early-strength Portland cement clinker ground product, percentage content of the limestone powder is 8 to 40 mass%, Blaine specific surface area is 4,500 cm/g or less, 90% vol.% cumulative particle diameter is 57 μm or less and 50 vol.% cumulative particle diameter is 22 μm or less.SELECTED DRAWING: None
【課題】左官用モルタルとして使用する際に、特殊な石灰石微粉末を使用しなくても、作業性が良好であり、かつ、壁面等に塗付けた後のモルタルの垂れの評価（ダレ難さ）が良好である、左官用粉末状セメント組成物を提供する。【解決手段】クリンカ粉砕物、石灰石粉末および石膏を含む左官用粉末状セメント組成物であって、クリンカ粉砕物が、普通ポルトランドセメントクリンカ粉砕物または早強ポルトランドセメントクリンカ粉砕物であり、石灰石粉末の含有率が８〜４０質量％であり、ブレーン比表面積が４，５００ｃｍ２／ｇ以下であり、９０体積％累積粒径が５７μｍ以下であり、５０体積％累積粒径が２２μｍ以下である、左官用粉末状セメント組成物。【選択図】なし
POWDERY CEMENT COMPOSITION FOR PLASTERER AND MORTAR FOR PLASTERER
左官用粉末状セメント組成物および左官用モルタル
KIRINO YUSUKE (Autor:in) / KUBOTA OSAMU (Autor:in) / HAYASHI KENSUKE (Autor:in) / KUROKAWA DAISUKE (Autor:in) / HIRAO HIROSHI (Autor:in)
06.04.2017
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
POWDERY CEMENT COMPOSITION FOR PLASTERER AND MORTAR FOR PLASTERER
| Europäisches Patentamt | 2017
METHOD FOR PRODUCING HYDRAULIC COMPOSITION FOR PLASTERER
| Europäisches Patentamt | 2020