MANUFACTURING METHOD OF HIGH-EARLY-STRENGTH LIGHT WEIGHT CONCRETE
PROBLEM TO BE SOLVED: To provide a manufacturing method of high-early-strength light weight concrete having light weight, small in autogenous shrinkage and capable of providing sufficient compressive strength with short curing term without using expensive materials and without using a specific method.SOLUTION: High-early-strength Portland cement (high-early-strength Portland cement defined in JIS R5210) is used as cement, an artificial light weight coarse aggregate with absolute dry density of 1.0 g/cmor more and less than 1.5 g/cmis used as the light weight coarse aggregate, unit cement content is 350 to 500 kg/m, water/cement ratio is 35 o 45 wt.%, normal fine aggregate amount is 600 o 920 kg/mand light weight coarse aggregate amount is 400 to 800 kg/m.SELECTED DRAWING: None
【課題】高価な材料を用いることなく、また、特殊な方法を採用することなく、軽量で、自己収縮が小さく、かつ、短い養生期間で十分な圧縮強度を得ることができる早強性軽量コンクリートの製造方法等を提供する。【解決手段】セメントとして、早強ポルトランドセメント（ＪＩＳ Ｒ５２１０に規定される早強ポルトランドセメント）を使用し、軽量粗骨材として、絶乾密度が１．０ｇ／ｃｍ３以上１．５ｇ／ｃｍ３未満の人工軽量粗骨材を使用し、単位セメント量を３５０〜５００ｋｇ／ｍ３とし、水／セメント比を３５〜４５重量％とし、普通細骨材量を６００〜９２０ｋｇ／ｍ３とし、軽量粗骨材量を４００〜８００ｋｇ／ｍ３とする。【選択図】なし
MANUFACTURING METHOD OF HIGH-EARLY-STRENGTH LIGHT WEIGHT CONCRETE
PROBLEM TO BE SOLVED: To provide a manufacturing method of high-early-strength light weight concrete having light weight, small in autogenous shrinkage and capable of providing sufficient compressive strength with short curing term without using expensive materials and without using a specific method.SOLUTION: High-early-strength Portland cement (high-early-strength Portland cement defined in JIS R5210) is used as cement, an artificial light weight coarse aggregate with absolute dry density of 1.0 g/cmor more and less than 1.5 g/cmis used as the light weight coarse aggregate, unit cement content is 350 to 500 kg/m, water/cement ratio is 35 o 45 wt.%, normal fine aggregate amount is 600 o 920 kg/mand light weight coarse aggregate amount is 400 to 800 kg/m.SELECTED DRAWING: None
【課題】高価な材料を用いることなく、また、特殊な方法を採用することなく、軽量で、自己収縮が小さく、かつ、短い養生期間で十分な圧縮強度を得ることができる早強性軽量コンクリートの製造方法等を提供する。【解決手段】セメントとして、早強ポルトランドセメント（ＪＩＳ Ｒ５２１０に規定される早強ポルトランドセメント）を使用し、軽量粗骨材として、絶乾密度が１．０ｇ／ｃｍ３以上１．５ｇ／ｃｍ３未満の人工軽量粗骨材を使用し、単位セメント量を３５０〜５００ｋｇ／ｍ３とし、水／セメント比を３５〜４５重量％とし、普通細骨材量を６００〜９２０ｋｇ／ｍ３とし、軽量粗骨材量を４００〜８００ｋｇ／ｍ３とする。【選択図】なし
MANUFACTURING METHOD OF HIGH-EARLY-STRENGTH LIGHT WEIGHT CONCRETE
早強性軽量コンクリートの製造方法
DANSHITA YOSHINORI (Autor:in) / KITANO YUICHI (Autor:in) / TAKADA YOSHIHIDE (Autor:in)
29.06.2017
Patent
Elektronische Ressource
Japanisch
High Strength Light Weight Aggregate Concrete
| British Library Conference Proceedings | 1996
Light-weight slag concrete develops high strength
| Engineering Index Backfile | 1935
Structural light weight concrete of high strength
| Engineering Index Backfile | 1964
High-strength light-weight concrete and preparation method thereof
| Europäisches Patentamt | 2015
Chloride Diffusivity of High Strength Light-Weight Concrete
| British Library Conference Proceedings | 1993