RAPID HARDENING MORTAR COMPOSITION
PROBLEM TO BE SOLVED: To provide a rapid hardening mortar composition which shows small fluctuation in setting starting time by an environmental temperature, has small fluctuation in setting starting time even stored for a long period of time, has high flowability for a period until a hardening reaction progresses after water is added, and is excellent in initial strength development property.SOLUTION: A rapid hardening mortar composition contains a rapid hardening admixture and 100 pts.mass or more and 2,000 pts.mass or less of cement with respect to 100 pts.mass of the rapid hardening admixture, where the rapid hardening admixture is a composition which contains calcium aluminate, 50 pts.mass or more and 200 pts.mass or less of inorganic sulfate with respect to 100 pts.mass of the calcium aluminate and 0.1 pt.mass or more and 10 pts.mass or less of a setting modifier with respect to 100 pts.mass of the calcium aluminate, an average particle diameter of the calcium aluminate is in a range of 8 μm or more and 100 μm or less, and an average particle diameter of the setting modifier is 5 μm or less.SELECTED DRAWING: None
【課題】環境温度による凝結始発時間の変動が小さく、長期間保存しても凝結始発時間の変動が小さく、水を加えてから硬化反応が進行するまでの間の流動性が高く、かつ初期強度発現性に優れる速硬性セメント組成物を提供する。【解決手段】速硬性混和材と、前記速硬性混和材１００質量部に対して１００質量部以上２０００質量部以下の範囲の量のセメントとを含む速硬性セメント組成物であって、前記速硬性混和材が、カルシウムアルミネートと、前記カルシウムアルミネート１００質量部に対して５０質量部以上２００質量部以下の範囲の量の無機硫酸塩と、前記カルシウムアルミネート１００質量部に対して０．１質量部以上１０質量部以下の範囲の量の凝結調整剤とを含む組成物であって、前記カルシウムアルミネートの平均粒子径が８μｍ以上１００μｍ以下の範囲にあり、前記凝結調整剤の平均粒子径が５μｍ以下であることを特徴とする速硬性セメント組成物。【選択図】なし
RAPID HARDENING MORTAR COMPOSITION
PROBLEM TO BE SOLVED: To provide a rapid hardening mortar composition which shows small fluctuation in setting starting time by an environmental temperature, has small fluctuation in setting starting time even stored for a long period of time, has high flowability for a period until a hardening reaction progresses after water is added, and is excellent in initial strength development property.SOLUTION: A rapid hardening mortar composition contains a rapid hardening admixture and 100 pts.mass or more and 2,000 pts.mass or less of cement with respect to 100 pts.mass of the rapid hardening admixture, where the rapid hardening admixture is a composition which contains calcium aluminate, 50 pts.mass or more and 200 pts.mass or less of inorganic sulfate with respect to 100 pts.mass of the calcium aluminate and 0.1 pt.mass or more and 10 pts.mass or less of a setting modifier with respect to 100 pts.mass of the calcium aluminate, an average particle diameter of the calcium aluminate is in a range of 8 μm or more and 100 μm or less, and an average particle diameter of the setting modifier is 5 μm or less.SELECTED DRAWING: None
【課題】環境温度による凝結始発時間の変動が小さく、長期間保存しても凝結始発時間の変動が小さく、水を加えてから硬化反応が進行するまでの間の流動性が高く、かつ初期強度発現性に優れる速硬性セメント組成物を提供する。【解決手段】速硬性混和材と、前記速硬性混和材１００質量部に対して１００質量部以上２０００質量部以下の範囲の量のセメントとを含む速硬性セメント組成物であって、前記速硬性混和材が、カルシウムアルミネートと、前記カルシウムアルミネート１００質量部に対して５０質量部以上２００質量部以下の範囲の量の無機硫酸塩と、前記カルシウムアルミネート１００質量部に対して０．１質量部以上１０質量部以下の範囲の量の凝結調整剤とを含む組成物であって、前記カルシウムアルミネートの平均粒子径が８μｍ以上１００μｍ以下の範囲にあり、前記凝結調整剤の平均粒子径が５μｍ以下であることを特徴とする速硬性セメント組成物。【選択図】なし
RAPID HARDENING MORTAR COMPOSITION
速硬性セメント組成物