ZEOLITE SEPARATION MEMBRANE AND MANUFACTURING METHOD THEREOF

YAMADA NAOKI / IGA YUTA

PROBLEM TO BE SOLVED: To provide: a zeolite separation membrane whose separation performance does not deteriorate easily; and a manufacturing method thereof.SOLUTION: After sticking a slurry containing seed crystals of and a growth inhibiting substance 9 for zeolite to a surface of a porous support body 3, a zeolite separation membrane 5 is formed from the seed crystals of zeolite by a hydrothermal synthesis using a synthetic fluid including a raw material of zeolite. Thus, when growing crystals of zeolite, a particulate growth inhibiting substance 9 inhibits oriented growth of the crystals of zeolite. Thus, since the crystals of zeolite are inhibited from oriented-growing in the predetermined direction (one direction), the zeolite separation membrane 5 manufactured in this way hardly generates through-holes even when grain boundaries of the crystals dissolve while using the zeolite separation membrane 5. Thus, separation performance of the zeolite separation membrane 5 does not deteriorate easily.SELECTED DRAWING: Figure 6

【課題】分離性能が低下し難いゼオライト分離膜及びその製造方法を提供すること。【解決手段】多孔質の支持体３の表面に、ゼオライトの種結晶及び成長抑制物質９を含むスラリーを付着させた後に、ゼオライトの原料を含む合成液を用いた水熱合成によって、ゼオライトの種結晶からゼオライト分離膜５を形成する。そのため、ゼオライトの結晶を成長させる際には、粒子状の成長抑制物質９が、ゼオライトの結晶の配向成長を抑制する。これによって、ゼオライトの結晶が所定の方向（一方向）に配向成長することが抑制されるので、このようにして製造されたゼオライト分離膜５は、ゼオライト分離膜５を使用しているうちに、結晶の粒界が溶解した場合でも貫通孔が生じにくい。そのため、ゼオライト分離膜５の分離性能が低下し難い。【選択図】図６

Zugriff

Download

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren