PROBLEM TO BE SOLVED: To provide a technology for using, for a resin sash, polyvinyl chloride powder having various types of polymerization degrees.SOLUTION: A method for producing a resin sash includes: mixing polyvinyl chloride powder containing 60 mass% or more of polyvinyl chloride having a polymerization degree of 1000 with an additive agent to produce a kneaded mixture; and extruding the kneaded mixture. In this configuration, the polyvinyl chloride powder containing 60 mass% or more of polyvinyl chloride having the polymerization degree of 1000 is used, so that fluidity adequate for extrusion is easily obtained and a resin sash can be successfully molded. Furthermore, addition of the additive agent to the polyvinyl chloride powder enables the polyvinyl chloride powder to have the component suitable for the resin sash.SELECTED DRAWING: Figure 4
【課題】種々の重合度を有するポリ塩化ビニル粉末を樹脂サッシに用いるための技術を提供する。【解決手段】樹脂サッシの製造方法では、重合度が１０００のポリ塩化ビニルを６０質量％以上含有するポリ塩化ビニル粉末と、添加剤と、を混合して混練物が作製される。前記混練物が押出成形される。この構成では、重合度が１０００のポリ塩化ビニルを６０質量％以上含有するポリ塩化ビニル粉末を用いることにより、押出成形する際に適切な流動性が得られやすく、樹脂サッシを良好に成形することが可能となる。また、ポリ塩化ビニル粉末に添加剤を添加することにより、樹脂サッシに適した成分に調整することが可能である。【選択図】図４
PROBLEM TO BE SOLVED: To provide a technology for using, for a resin sash, polyvinyl chloride powder having various types of polymerization degrees.SOLUTION: A method for producing a resin sash includes: mixing polyvinyl chloride powder containing 60 mass% or more of polyvinyl chloride having a polymerization degree of 1000 with an additive agent to produce a kneaded mixture; and extruding the kneaded mixture. In this configuration, the polyvinyl chloride powder containing 60 mass% or more of polyvinyl chloride having the polymerization degree of 1000 is used, so that fluidity adequate for extrusion is easily obtained and a resin sash can be successfully molded. Furthermore, addition of the additive agent to the polyvinyl chloride powder enables the polyvinyl chloride powder to have the component suitable for the resin sash.SELECTED DRAWING: Figure 4
【課題】種々の重合度を有するポリ塩化ビニル粉末を樹脂サッシに用いるための技術を提供する。【解決手段】樹脂サッシの製造方法では、重合度が１０００のポリ塩化ビニルを６０質量％以上含有するポリ塩化ビニル粉末と、添加剤と、を混合して混練物が作製される。前記混練物が押出成形される。この構成では、重合度が１０００のポリ塩化ビニルを６０質量％以上含有するポリ塩化ビニル粉末を用いることにより、押出成形する際に適切な流動性が得られやすく、樹脂サッシを良好に成形することが可能となる。また、ポリ塩化ビニル粉末に添加剤を添加することにより、樹脂サッシに適した成分に調整することが可能である。【選択図】図４
METHOD FOR PRODUCING RESIN SASH
樹脂サッシの製造方法
SHIMOYAMA HIDEO (Autor:in)
19.04.2018
Patent
Elektronische Ressource
Japanisch
IPC:
E06B
Feste oder bewegliche Abschlüsse für Öffnungen in Bauwerken, Fahrzeugen, Zäunen oder ähnlichen Einfriedungen allgemein, z.B. Türen, Fenster, Läden, Tore
,
FIXED OR MOVABLE CLOSURES FOR OPENINGS IN BUILDINGS, VEHICLES, FENCES, OR LIKE ENCLOSURES, IN GENERAL, e.g. DOORS, WINDOWS, BLINDS, GATES
/
B29B
PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED
,
Vorbereiten oder Vorbehandeln der zu verformenden Masse
COMPOSITION FOR SASH, SASH, AND METHOD FOR PRODUCING SASH