HYDRAULIC COMPOSITION FOR CENTRIFUGAL MOLDING
PROBLEM TO BE SOLVED: To provide a hydraulic composition which gives by centrifugal molding a hardened article having high strength and also has excellent moldability.SOLUTION: The hydraulic composition for centrifugal molding contains (A) one or more compound selected from sulfamic acid and a sulfamate (hereafter, A component), a hydraulic powder, an aggregate, and water, wherein the content of the A component is 0.01-0.2 pts.mass per 100 pts.mass of the hydraulic powder. Moreover, 0.5-1.0 pts.mass of a naphthalenesulfonic acid-formaldehyde condensate or a salt thereof (hereafter, B component) is preferably contained per 100 pts.mass of the hydraulic powder. Moreover, the hydraulic composition for centrifugal molding preferably contains 0.01-0.2 pts.mass of glycerin (hereafter, C component) per 100 pts.mass of the hydraulic powder, and 0.001-0.1 pt.mass of one or more compound selected from sucrose, gluconic acid, and a gluconate (hereafter, D component).SELECTED DRAWING: None
【課題】遠心成型による硬化体が高強度で、且つ成型性にも優れた水硬性組成物の提供。【解決手段】（Ａ）スルファミン酸、及びスルファミン酸塩から選ばれる１種以上の化合物〔以下、（Ａ）成分という〕と、水硬性粉体と、骨材と、水とを含有し、（Ａ）成分の含有量が水硬性粉体１００質量部に対して０．０１〜０．２質量部である、遠心成型用水硬性組成物。さらに、ナフタレンスルホン酸ホルムアルデヒド縮合物又はその塩〔（B）成分という〕を水硬性粉体１００質量部に対して０．５〜１．０質量部含有することが更に好ましい。その上、グリセリン〔（Ｂ）成分という〕を水硬性粉体１００質量部に対して、０．０１〜０．２質量部、スクロース、グルコン酸及びグルコン酸塩から選ばれる一種以上の化合物〔（Ｄ）成分という〕を０．００１〜０．１質量部含有することが好ましい、遠心成型用水硬性組成物。【選択図】なし
HYDRAULIC COMPOSITION FOR CENTRIFUGAL MOLDING
PROBLEM TO BE SOLVED: To provide a hydraulic composition which gives by centrifugal molding a hardened article having high strength and also has excellent moldability.SOLUTION: The hydraulic composition for centrifugal molding contains (A) one or more compound selected from sulfamic acid and a sulfamate (hereafter, A component), a hydraulic powder, an aggregate, and water, wherein the content of the A component is 0.01-0.2 pts.mass per 100 pts.mass of the hydraulic powder. Moreover, 0.5-1.0 pts.mass of a naphthalenesulfonic acid-formaldehyde condensate or a salt thereof (hereafter, B component) is preferably contained per 100 pts.mass of the hydraulic powder. Moreover, the hydraulic composition for centrifugal molding preferably contains 0.01-0.2 pts.mass of glycerin (hereafter, C component) per 100 pts.mass of the hydraulic powder, and 0.001-0.1 pt.mass of one or more compound selected from sucrose, gluconic acid, and a gluconate (hereafter, D component).SELECTED DRAWING: None
【課題】遠心成型による硬化体が高強度で、且つ成型性にも優れた水硬性組成物の提供。【解決手段】（Ａ）スルファミン酸、及びスルファミン酸塩から選ばれる１種以上の化合物〔以下、（Ａ）成分という〕と、水硬性粉体と、骨材と、水とを含有し、（Ａ）成分の含有量が水硬性粉体１００質量部に対して０．０１〜０．２質量部である、遠心成型用水硬性組成物。さらに、ナフタレンスルホン酸ホルムアルデヒド縮合物又はその塩〔（B）成分という〕を水硬性粉体１００質量部に対して０．５〜１．０質量部含有することが更に好ましい。その上、グリセリン〔（Ｂ）成分という〕を水硬性粉体１００質量部に対して、０．０１〜０．２質量部、スクロース、グルコン酸及びグルコン酸塩から選ばれる一種以上の化合物〔（Ｄ）成分という〕を０．００１〜０．１質量部含有することが好ましい、遠心成型用水硬性組成物。【選択図】なし
HYDRAULIC COMPOSITION FOR CENTRIFUGAL MOLDING
遠心成型用水硬性組成物
OMAE TOMOYA (Autor:in) / AKINO TAKEAKI (Autor:in) / OKAUCHI NOBUAKI (Autor:in)
21.06.2018
Patent