PROBLEM TO BE SOLVED: To provide a refractory composition having no need for increasing height of a beam and no need for making a reinforcement part of an open hole large-sized in a heat resistant coating of a beam open pore.SOLUTION: There is provided a heat expansion refractory composition which is used for a heat resistant coating material of an iron frame beam open pore small lot and expands at heating, contains a rubber resin or a thermoplastic resin of 100 pts.wt., a heat expansion component expanding at heating of 2 to 30 pts.wt., boric acid of 70 to 250 pts.wt. and aluminum oxide, and has a weight ratio of the aluminum oxide and the boric acid (aluminum oxide/boric acid) of 0.45 to 1.5, and total content of a silicate compound, a magnesium salt and a calcium salt of 0% or more and less than 10% by mass ratio to the boric acid.SELECTED DRAWING: Figure 1
【課題】梁貫通孔の耐火被覆において、はりせいを大きくする必要がなく、また貫通孔の補強部材を大型のものにする必要のない耐火被覆材を提供することを目的とする。【解決手段】鉄骨梁貫通孔小口の耐火被覆材に用いられ、加熱時に膨張する熱膨張性耐火組成物であって、ゴム系樹脂または熱可塑性樹脂１００重量部と、加熱時に膨張する熱膨張成分２〜３０重量部と、ホウ酸７０〜２５０重量部と、酸化アルミニウムとを含有し、酸化アルミニウムとホウ酸に対する重量比（酸化アルミニウム／ホウ酸）が０．４５以上１．５以下であり、ケイ酸化合物、マグネシウム塩およびカルシウム塩の合計含有量が、ホウ酸に対して質量比で０％以上１０％未満であることを特徴とする、熱膨張性耐火組成物。【選択図】図１
PROBLEM TO BE SOLVED: To provide a refractory composition having no need for increasing height of a beam and no need for making a reinforcement part of an open hole large-sized in a heat resistant coating of a beam open pore.SOLUTION: There is provided a heat expansion refractory composition which is used for a heat resistant coating material of an iron frame beam open pore small lot and expands at heating, contains a rubber resin or a thermoplastic resin of 100 pts.wt., a heat expansion component expanding at heating of 2 to 30 pts.wt., boric acid of 70 to 250 pts.wt. and aluminum oxide, and has a weight ratio of the aluminum oxide and the boric acid (aluminum oxide/boric acid) of 0.45 to 1.5, and total content of a silicate compound, a magnesium salt and a calcium salt of 0% or more and less than 10% by mass ratio to the boric acid.SELECTED DRAWING: Figure 1
【課題】梁貫通孔の耐火被覆において、はりせいを大きくする必要がなく、また貫通孔の補強部材を大型のものにする必要のない耐火被覆材を提供することを目的とする。【解決手段】鉄骨梁貫通孔小口の耐火被覆材に用いられ、加熱時に膨張する熱膨張性耐火組成物であって、ゴム系樹脂または熱可塑性樹脂１００重量部と、加熱時に膨張する熱膨張成分２〜３０重量部と、ホウ酸７０〜２５０重量部と、酸化アルミニウムとを含有し、酸化アルミニウムとホウ酸に対する重量比（酸化アルミニウム／ホウ酸）が０．４５以上１．５以下であり、ケイ酸化合物、マグネシウム塩およびカルシウム塩の合計含有量が、ホウ酸に対して質量比で０％以上１０％未満であることを特徴とする、熱膨張性耐火組成物。【選択図】図１
HEAT EXPANSION REFRACTORY COMPOSITION
熱膨張性耐火組成物
KATO MASARU (Autor:in)
27.09.2018
Patent
Elektronische Ressource
Japanisch
IPC:
C09K
Materialien für Anwendungen, soweit nicht anderweitig vorgesehen
,
MATERIALS FOR APPLICATIONS NOT OTHERWISE PROVIDED FOR
/
C08K
Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe
,
USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
/
C08L
COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
,
Massen auf Basis makromolekularer Verbindungen
/
E04B
Allgemeine Baukonstruktionen
,
GENERAL BUILDING CONSTRUCTIONS
| Europäisches Patentamt | 2023
Expansion of refractory materials
| Engineering Index Backfile | 1956
REFRACTORY COATING COMPOSITION INCLUDING NOVEL HEAT-RESISTANT MATERIALS
| Europäisches Patentamt | 2017