FAST CURING ADMIXTURE
To provide a fast curing admixture which has high effects of increasing initial strength of a cement composition and preventing occurrence of white spots, these effects being hard to deteriorate even when stored for a long term.SOLUTION: The fast curing admixture comprises calcium aluminate, anhydrous gypsum, inorganic carbonate, oxycarboxylic acid, and alum, where calcium aluminate has a CaO content relative to Al2O3 of 1.50 to 2.0 in a molar ratio and a vitrification ratio of 80% or more, a content of anhydrous gypsum is in a range of 35 to 65 pts.mass relative to a total amount of calcium aluminate and anhydrous gypsum of 100 pts.mass, contents of inorganic carbonate, oxycarboxylic acid, and alum are respectively 0.1 pts.mass or more relative to a total of calcium aluminate and anhydrous gypsum of 100 pts.mas, and a total content of inorganic carbonate, oxycarboxylic acid, and alum is 10 pts.mass or less relative to a total amount of calcium aluminate and anhydrous gypsum of 100 pts.mass.SELECTED DRAWING: None
【課題】セメント組成物の初期強度を高める作用と、白斑の発生を防止する作用とが高く、かつこれらの作用が長期間保存しても低下しにくい速硬性混和材を提供する。【解決手段】カルシウムアルミネートと無水石膏と無機炭酸塩とオキシカルボン酸とミョウバンとを含み、カルシウムアルミネートはＡｌ２Ｏ３に対するＣａＯの含有量がモル比で１．５０〜２．０の範囲内にあって、ガラス化率が８０％以上であり、無水石膏の含有量はカルシウムアルミネートと無水石膏の合計量１００質量部に対して３５〜６５質量部の範囲内にあって、無機炭酸塩、オキシカルボン酸及びミョウバンの含有量は、それぞれカルシウムアルミネートと無水石膏の合計量１００質量部に対して０．１質量部以上であって、無機炭酸塩、オキシカルボン酸及びミョウバンの合計含有量は、カルシウムアルミネートと無水石膏の合計量１００質量部に対して１０質量部以下である速硬性混和材。【選択図】なし
FAST CURING ADMIXTURE
To provide a fast curing admixture which has high effects of increasing initial strength of a cement composition and preventing occurrence of white spots, these effects being hard to deteriorate even when stored for a long term.SOLUTION: The fast curing admixture comprises calcium aluminate, anhydrous gypsum, inorganic carbonate, oxycarboxylic acid, and alum, where calcium aluminate has a CaO content relative to Al2O3 of 1.50 to 2.0 in a molar ratio and a vitrification ratio of 80% or more, a content of anhydrous gypsum is in a range of 35 to 65 pts.mass relative to a total amount of calcium aluminate and anhydrous gypsum of 100 pts.mass, contents of inorganic carbonate, oxycarboxylic acid, and alum are respectively 0.1 pts.mass or more relative to a total of calcium aluminate and anhydrous gypsum of 100 pts.mas, and a total content of inorganic carbonate, oxycarboxylic acid, and alum is 10 pts.mass or less relative to a total amount of calcium aluminate and anhydrous gypsum of 100 pts.mass.SELECTED DRAWING: None
【課題】セメント組成物の初期強度を高める作用と、白斑の発生を防止する作用とが高く、かつこれらの作用が長期間保存しても低下しにくい速硬性混和材を提供する。【解決手段】カルシウムアルミネートと無水石膏と無機炭酸塩とオキシカルボン酸とミョウバンとを含み、カルシウムアルミネートはＡｌ２Ｏ３に対するＣａＯの含有量がモル比で１．５０〜２．０の範囲内にあって、ガラス化率が８０％以上であり、無水石膏の含有量はカルシウムアルミネートと無水石膏の合計量１００質量部に対して３５〜６５質量部の範囲内にあって、無機炭酸塩、オキシカルボン酸及びミョウバンの含有量は、それぞれカルシウムアルミネートと無水石膏の合計量１００質量部に対して０．１質量部以上であって、無機炭酸塩、オキシカルボン酸及びミョウバンの合計含有量は、カルシウムアルミネートと無水石膏の合計量１００質量部に対して１０質量部以下である速硬性混和材。【選択図】なし
FAST CURING ADMIXTURE
速硬性混和材
KIMOTO DAISUKE (Autor:in) / INOHANA HITOSHI (Autor:in) / TAKAHARA KONOSUKE (Autor:in) / SAITO KEIJI (Autor:in) / FUKUSHIMA YUICHI (Autor:in) / KAMIYA KIYOSHI (Autor:in)
08.10.2020
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
| British Library Online Contents | 2012
Self Curing Admixture Performance Report
| NTIS | 2012
| Europäisches Patentamt | 2024
Curing cement concrete by using shrinkage reducing admixture and curing compound
| Online Contents | 2013