MANUFACTURING METHOD OF CEMENT-BASED HARDENED BODY
To solve the problem that the cement-based hardened body are subject to efflorescence due to carbonation caused by the elution of free lime on the surface, and the amount of an efflorescence inhibitor used to suppress the efflorescence increases, resulting in an increase in the production cost of cement-based hardened bodies, and to provide a method for producing the cement-based hardened body with the reduced amount of the efflorescence inhibitor for suppressing efflorescence.SOLUTION: In a cement-based hardened body of this invention in which an aggregate, a cementitious binder, water, and an efflorescence inhibitor are mixed and hardened, 0.5-1.4 mass times of granulated blast furnace slag aggregate is used in relation to the cementitious binder. Further, if the amount of granulated blast furnace slag aggregate used is within this range, other aggregate may be used in combination.SELECTED DRAWING: None
【課題】 セメント系硬化体は遊離石灰分が表面に溶出して炭酸化することで白華が発生するが、その抑制のために使用する白華防止剤の使用量が多くなり、セメント系硬化体の製造コストが増加することが課題であった。本発明は、白華抑制のための白華防止剤の添加量を少なくしたセメント系硬化体の製造方法を提供するものである。【解決手段】 骨材とセメント系結合材と水と白華防止剤とを混合、硬化させるセメント系硬化体において、セメント系結合材に対して０．５〜１．４質量倍の高炉水砕スラグ骨材を用いる。なお、高炉水砕スラグ骨材の使用量がこの範囲であれば、他の骨材を併用してもよい。【選択図】 なし
MANUFACTURING METHOD OF CEMENT-BASED HARDENED BODY
To solve the problem that the cement-based hardened body are subject to efflorescence due to carbonation caused by the elution of free lime on the surface, and the amount of an efflorescence inhibitor used to suppress the efflorescence increases, resulting in an increase in the production cost of cement-based hardened bodies, and to provide a method for producing the cement-based hardened body with the reduced amount of the efflorescence inhibitor for suppressing efflorescence.SOLUTION: In a cement-based hardened body of this invention in which an aggregate, a cementitious binder, water, and an efflorescence inhibitor are mixed and hardened, 0.5-1.4 mass times of granulated blast furnace slag aggregate is used in relation to the cementitious binder. Further, if the amount of granulated blast furnace slag aggregate used is within this range, other aggregate may be used in combination.SELECTED DRAWING: None
【課題】 セメント系硬化体は遊離石灰分が表面に溶出して炭酸化することで白華が発生するが、その抑制のために使用する白華防止剤の使用量が多くなり、セメント系硬化体の製造コストが増加することが課題であった。本発明は、白華抑制のための白華防止剤の添加量を少なくしたセメント系硬化体の製造方法を提供するものである。【解決手段】 骨材とセメント系結合材と水と白華防止剤とを混合、硬化させるセメント系硬化体において、セメント系結合材に対して０．５〜１．４質量倍の高炉水砕スラグ骨材を用いる。なお、高炉水砕スラグ骨材の使用量がこの範囲であれば、他の骨材を併用してもよい。【選択図】 なし
MANUFACTURING METHOD OF CEMENT-BASED HARDENED BODY
セメント系硬化体の製造方法
NIIMI TATSUO (Autor:in) / KATO HIROYOSHI (Autor:in) / TSUKUDA YOSHINOBU (Autor:in) / KURODA TAKAAKI (Autor:in) / IWAMOTO MASATO (Autor:in)
09.09.2021
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
CEMENT HARDENED BODY PRODUCTION METHOD AND CEMENT HARDENED BODY
| Europäisches Patentamt | 2024
CEMENT COMPOSITION, AND MANUFACTURING METHOD CEMENT HARDENED BODY
| Europäisches Patentamt | 2021
CEMENT COMPOSITION, AND MANUFACTURING METHOD OF CEMENT HARDENED BODY
| Europäisches Patentamt | 2019
MOLDING CEMENT COMPOSITION AND MANUFACTURING METHOD OF CEMENT HARDENED BODY
| Europäisches Patentamt | 2021